LNP™ ELCRES™ FXM9111T

ELCRES FXM9111T PC-siloxane copolymer resin is an injection molding grade. Non-chlorinated, non-brominated flame retardant product. This resin offers room temp ductility in combination with high flow characteristics and excellent processability with opportunities for shorter injection molding cycle times comparing to standard PC. Available for VisualFx capability in “metallic” colors: sparkle appearance featured. Fine metallic appearance is limited. ELCRES FXM9111T resin may be an excellent candidate for a broad range of applications, including but not limited to Automotive, Appliances, Electronics, etc. Color package may affect performance.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Aesthetics/Visual effects
No PFAS intentionally added

Industry

Material previously used in

Automotive Interiors
Commercial Appliance
Consumer Goods
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Commercial Appliance
Electronics
Enclosure/Housing/Cover
Interior

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	≥2.5	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	425	J/m	ASTM D256
*Izod Impact, notched 80104 +23°C*	33	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	180	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	36	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	130	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	90	°C
Drying Time	3 - 4	Hrs
Nozzle Temperature	250 - 285	°C
Front - Zone 3 Temperature	250 - 285	°C
Middle - Zone 2 Temperature	250 - 285	°C
Rear - Zone 1 Temperature	250 - 285	°C
Mold Temperature	50 - 90	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	58	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	50	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	67	%	ASTM D638
Tensile Modulus, 50 mm/min	2400	MPa	ASTM D638
Flexural Stress at 5% strain, 1.3 mm/min, 50 mm span	83	MPa	ASTM D790
Flexural Strength, 1.3 mm/min, 50 mm span	89	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2170	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	60	MPa	ISO 527
Tensile Stress, break, 50 mm/min	48	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5	%	ISO 527
Tensile Strain, break, 50 mm/min	74	%	ISO 527
Tensile Modulus, 1 mm/min	2480	MPa	ISO 527
Flexural Stress at 3.5% strain, 2 mm/min	60.8	MPa	ISO 178
Flexural Strain, break, 2 mm/min	9.2	%	ISO 178
Flexural Strength, 2 mm/min	87	MPa	ISO 178
Flexural Modulus, 2 mm/min	1877	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.2	-	ASTM D792
Density	1.2	g/cm³	ISO 1183
Water Absorption, (23°C/24hrs)	0.12	%	ISO 62-1
Moisture Absorption, (23°C/50% RH/24hrs)	0.04	%	ISO 62-4
Melt Flow Rate, 300°C/1.2 kgf	18.5	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 300°C/1.2 kg	17.7	cm³/10 min	ASTM D1238
Mold Shrinkage, flow	0.51	%	SABIC method
Mold Shrinkage, xflow	0.5	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	122	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	110	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	122	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	110	°C	ISO 75/Af
CTE, -40°C to 95°C, flow	7.50E-05	1/°C	ASTM E831
CTE, -40°C to 95°C, xflow	8.04E-05	1/°C	ASTM E831
CTE, 23°C to 80°C, flow	8.01E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	8.51E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate A/50	127	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	127	°C	ASTM D1525
Vicat Softening Temp, Rate B/50	128	°C	ISO 306
Vicat Softening Temp, Rate B/120	127	°C	ISO 306
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience