LNP ELCRES NPCRX9612U is an unfilled, amorphous polycarbonate (PC) copolymer resin for injection moulding. This grade is a non-chlorinated, non-brominated flame-retardant grade, having a UL-94 V0 rating at 1.5 mm, for “All colours” and certified per UL746G - an outline of investigation for non-fluorine and non-PFAS containing materials. The grade is UV stabilized and is available for custom colouring. The material has improved chemical resistance against a wide range of disinfectants and targets a wide variety of medical equipment applications that need improved chemical durability. The grade has passed the limited biocompatibility tests as per ISO 10993-5 and ISO 10993-10.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Recognized | |||
| – UL 746G certificate | https://iq.ul.com/cert/cofc.aspx?ULID=104695362 | - | UL Tested |
| UL Yellow Card Link | View | - | - |
| UL94 Flame Class Rating | |||
| – UL Recognized, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 |
| – UL Recognized, 94V-0 Flame Class Rating | 3.0 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 62 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 0°C | 63 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 59 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*3 +23°C | 65 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 56 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*3 +23°C | 120 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*3 -30°C | 140 | kJ/m² | ISO 180/1U |
| Izod Impact, notched, 23°C | 900 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 825 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | NB | J/m | ASTM D4812 |
| Izod Impact, unnotched, -30°C | NB | J/m | ASTM D4812 |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 70 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 60 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | 110 | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | 85 | kJ/m² | ISO 179/1eU |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2 - 4 | Hrs | |
| Drying Time (Cumulative) | 48 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 270 - 310 | °C | |
| Nozzle Temperature | 275 - 305 | °C | |
| Front - Zone 3 Temperature | 285 - 315 | °C | |
| Middle - Zone 2 Temperature | 275 - 305 | °C | |
| Rear - Zone 1 Temperature | 270 - 300 | °C | |
| Mold Temperature | 80 - 100 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 60 - 100 | rpm | |
| Shot to Cylinder Size | 40 - 60 | % | |
| Vent Depth | 0.025 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 50 mm/min | 54 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 63 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | >100 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2000 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 78 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2050 | MPa | ISO 178 |
| Tensile Stress, yld, Type I, 50 mm/min | 55 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 66 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | >100 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2050 | MPa | ASTM D638 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Specific Gravity | 1.19 | - | ASTM D792 |
| Mold Shrinkage, flow | 0.5 - 0.9 | % | SABIC method |
| Mold Shrinkage, xflow | 0.5 - 0.9 | % | SABIC method |
| Melt Volume Rate, MVR at 300°C/2.16 kg | 10 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 300°C/5.0 kg | 28 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 139 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 126 | °C | ISO 75/Af |
| Vicat Softening Temp, Rate B/50 | 144 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 144 | °C | ISO 306 |
| Vicat Softening Temp, Rate A/50 | 153 | °C | ISO 306 |
| Vicat Softening Temp, Rate A/120 | 152 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 144 | °C | ASTM D1525 |
| Vicat Softening Temp, Rate B/120 | 144 | °C | ASTM D1525 |
| Vicat Softening Temp, Rate A/50 | 153 | °C | ASTM D1525 |
| Vicat Softening Temp, Rate A/120 | 152 | °C | ASTM D1525 |
| CTE, 23°C to 50°C, flow | 7.7E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 50°C, xflow | 9.1E-05 | 1/°C | ISO 11359-2 |
| Relative Temp Index, Elec | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 105 | °C | UL 746B |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |