LNP™ ELCRES™ SD3038

LNP ELCRES SD3038 is a compound based on Copolymer Polycarbonate resin with good processability and excellent notched impact performance. This grade offers extreme enhanced Low Temperature Ductility (-70°C) and available for wide variety of applications.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Low temperature impact
No PFAS intentionally added

Industry

Material previously used in

Building Component
Electrical
Material Handling
Recreational/Specialty Vehicles

Applications

Possible usage of material

Electrical
Electronics
Enclosure/Housing/Cover
EV Infrastructure
Individual Equipment

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	>1.E+15	Ω	ASTM D257
Volume Resistivity	>1.E+15	Ω.cm	ASTM D257
Hot-Wire Ignition (HWI), PLC 0	≥0.7	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 1	≥0.7	mm	UL 746A

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94HB Flame Class Rating	≥0.4	mm	UL 94
UV-light, water exposure/immersion	f1	-	UL 746C

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	870	J/m	ASTM D256
Izod Impact, notched, -30°C	780	J/m	ASTM D256
Izod Impact, notched, -70°C	617	J/m	ASTM D256
*Izod Impact, notched 80103 +23°C*	72	kJ/m²	ISO 180/1A
*Izod Impact, notched 80103 -30°C*	62	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80103 +23°C*	NB	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80103 -30°C*	NB	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	72	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80103 sp=62mm*	65	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80103 sp=62mm*	NB	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80103 sp=62mm*	NB	kJ/m²	ISO 179/1eU
Instrumented Dart Impact Total Energy, 23°C	70	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	3 - 4	Hrs
Drying Time (Cumulative)	48	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	295 - 315	°C
Nozzle Temperature	290 - 310	°C
Front - Zone 3 Temperature	295 - 315	°C
Middle - Zone 2 Temperature	280 - 305	°C
Rear - Zone 1 Temperature	270 - 295	°C
Mold Temperature	70 - 95	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	56	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	52	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	6	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	100	%	ASTM D638
Tensile Modulus, 50 mm/min	2000	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	91	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2200	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	56	MPa	ISO 527
Tensile Stress, break, 50 mm/min	59	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	6	%	ISO 527
Tensile Strain, break, 50 mm/min	120	%	ISO 527
Tensile Modulus, 1 mm/min	2130	MPa	ISO 527
Flexural Strength, 2 mm/min	87	MPa	ISO 178
Flexural Modulus, 2 mm/min	2230	MPa	ISO 178
Hardness, Rockwell R	121	-	ASTM D785
Hardness, Rockwell L	89	-	ASTM D785

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.18	-	ASTM D792
Density	1.19	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.15	%	ISO 62
Water Absorption, (23°C/saturated)	0.35	%	ISO 62-1
Melt Flow Rate, 300°C/1.2 kgf	11	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 300°C/1.2 kg	9.5	cm³/10 min	ISO 1133
Mold Shrinkage, flow, 3.2 mm	0.4 - 0.8	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	0.4 - 0.8	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	139	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	124	°C	ASTM D648
*HDT/Be, 0.45MPa Edgew 120104 sp=100mm*	140	°C	ISO 75/Be
*HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm*	128	°C	ISO 75/Ae
CTE, -40°C to 40°C, flow	7.0E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	7.47E-05	1/°C	ASTM E831
CTE, 23°C to 80°C, flow	7.2E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	7.2E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	145	°C	ASTM D1525
Vicat Softening Temp, Rate B/50	145	°C	ISO 306
Vicat Softening Temp, Rate B/120	146	°C	ISO 306
Relative Temp Index, Elec	130	°C	UL 746B
Relative Temp Index, Mech w/impact	120	°C	UL 746B
Relative Temp Index, Mech w/o impact	130	°C	UL 746B
Ball Pressure Test, 125°C +/- 2°C	Passes	-	IEC 60695-10-2

Register for High value Multi-Point Data