LNP™ ELCRES™ SLX1291TIB

LNP ELCRES SLX1291TIB is based on Polycarbonate (PC) copolymer resin. It is an injection moldable, weatherable product that offers enhanced UV stabilization, impact durability and can reduce "interior" heat build up in the article or part by selectively blocking the near infra-red region of the sunlight. This medium flow (19 MFR) resin provides good processability with added mold release. SLX1291TIB is targeted for a broad range of electrical components in the Building and Construction, Industrial, Infrastructure, Medical Facility Infrastructure and Energy storage applications.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Aesthetics & Visual effects
Colorable
Ductile
Easy Flow
Enhanced Low Temperature Impact
Good Mold Release
Good Processability
No PFAS intentionally added
Transparent
Weatherable
Weatherable/UV stable

Industry

Material previously used in

Energy Storage
General Healthcare

Applications

Possible usage of material

Building Accessory
Building Element
Circuit Protection
Electrical Components & Infrastructure
Enclosure/Housing/Cover
Enclosures
Energy Absorber
Energy Management
Glazing
Infrastructure
Medical Device
Medical Facility Infrastructure
Power Manangement

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80103 +23°C*	60	kJ/m²	ISO 180/1A
*Izod Impact, notched 80103 0°C*	45	kJ/m²	ISO 180/1A
*Izod Impact, notched 80103 -30°C*	15	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	69	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80103 sp=62mm*	17	kJ/m²	ISO 179/1eA
Multi-Axial Instrumented Impact Total Energy, 23°C	84	J	ISO 6603-2
Multi-Axial Instrumented Impact Total Energy, -30°C	64	J	ISO 6603-2
Izod Impact, notched, 23°C	800	J/m	ASTM D256
Izod Impact, notched, 0°C	605	J/m	ASTM D256
Izod Impact, notched, -30°C	170	J/m	ASTM D256
*Izod Impact, unnotched 80103 +23°C*	172	kJ/m²	ISO 180/1U
*Charpy 23°C, Unnotch Edgew 80103 sp=62mm*	NB	kJ/m²	ISO 179/1eU
Izod Impact, unnotched, 23°C	NB	J/m	ASTM D4812

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110 - 120	°C
Drying Time	2 - 4	Hrs
Maximum Moisture Content	0.02	%
Hopper Temperature	40 - 80	°C
Melt Temperature	280 - 310	°C
Rear - Zone 1 Temperature	260 - 280	°C
Middle - Zone 2 Temperature	270 - 290	°C
Front - Zone 3 Temperature	280 - 310	°C
Nozzle Temperature	280 - 310	°C
Mold Temperature	80 - 120	°C
Back Pressure	3.0 - 10	MPa
Screw speed (Circumferential speed)	0.15 - 0.25	m/s

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 1 mm/min	2250	MPa	ISO 527
Tensile Stress, yield, 50 mm/min	60	MPa	ISO 527
Tensile Stress, break, 50 mm/min	59	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5.8	%	ISO 527
Tensile Strain, break, 50 mm/min	>100	%	ISO 527
Flexural Modulus, 2 mm/min	2300	MPa	ISO 178
Flexural Strength, 2 mm/min	94	MPa	ISO 178
Tensile Modulus, 5 mm/min	2275	MPa	ASTM D638
Tensile Stress, yld, Type I, 50 mm/min	62	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	55	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	6.0	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	69	%	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	2400	MPa	ASTM D790
Flexural Strength, 1.3 mm/min, 50 mm span	98	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.20	g/cm³	ISO 1183
Melt Volume Rate, MVR at 300°C/1.2 kg	19	cm³/10 min	ISO 1133
Specific Gravity	1.20	-	ASTM D792
Melt Flow Rate, 300°C/1.2 kgf	21	g/10 min	ASTM D1238
Mold Shrinkage, flow	0.6 - 0.8	%	SABIC method
Mold Shrinkage, xflow	0.6 - 0.8	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	120	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	133	°C	ISO 75/Bf
Vicat Softening Temp, Rate B/50	138	°C	ISO 306
Vicat Softening Temp, Rate B/120	140	°C	ISO 306
CTE, 23°C to 50°C, flow	6.8E-05	1/°C	ISO 11359-2
CTE, 23°C to 50°C, xflow	6.8E-05	1/°C	ISO 11359-2
HDT, 1.82 MPa, 3.2mm, unannealed	120	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	132	°C	ASTM D648
Vicat Softening Temp, Rate B/50	138	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	140	°C	ASTM D1525
CTE, 23°C to 50°C, flow	6.8E-05	1/°C	ASTM E831
CTE, 23°C to 50°C, xflow	6.8E-05	1/°C	ASTM E831

Register for High value Multi-Point Data