LNP ELCRES SLX1462T is based on Polycarbonate (PC) copolymer resin. It is an injection moldable, weatherable product that offers enhanced UV stabilization, improved scratch resistance and chemical resistance performance. Targeted for potential paint elimination through a wide range of transparent or opaque colors. SLX1462T is targeted for a broad range of automotive, electrical, consumer, and electronics applications.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 688 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 2130 | J/m | ASTM D4812 |
| Izod Impact, notched 80*10*3 +23°C | 19.1 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*3 +23°C | 141.7 | kJ/m² | ISO 180/1U |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 28 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | 102.5 | kJ/m² | ISO 179/1eU |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Melt Temperature | 280 - 320 | °C | |
| Nozzle Temperature | 280 - 320 | °C | |
| Front - Zone 3 Temperature | 280 - 320 | °C | |
| Middle - Zone 2 Temperature | 270 - 310 | °C | |
| Rear - Zone 1 Temperature | 260 - 300 | °C | |
| Mold Temperature | 50 - 110 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 50 mm/min | 65 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 66 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2366 | MPa | ASTM D638 |
| Flexural Strength, 1.3 mm/min, 50 mm span | 114 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2440 | MPa | ASTM D790 |
| Tensile Stress, break, 50 mm/min | 70 | MPa | ISO 527 |
| Tensile Strain, break, 50 mm/min | 84 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2366 | MPa | ISO 527 |
| Flexural Strength, 2 mm/min | 105 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2436 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.31 | - | ASTM D792 |
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Flow Rate, 300°C/1.2 kgf | 12 | g/10 min | ASTM D1238 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 11 | cm³/10 min | ISO 1133 |
| Mold Shrinkage, flow | 0.59 | % | SABIC method |
| Mold Shrinkage, xflow | 0.55 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 126 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 114 | °C | ASTM D648 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 126.1 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 113.6 | °C | ISO 75/Af |
| CTE, -40°C to 40°C, flow | 7.1E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 7.2E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 7.0E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.0E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 140 | °C | ASTM D1525 |
| Vicat Softening Temp, Rate B/50 | 133 | °C | ISO 306 |