LNP™ ELCRES™ SLX2291T

LNP ELCRES SLX2291T is based on Polycarbonate (PC) copolymer resin. It is an injection moldable, weatherable product that offers enhanced UV stabilization. This high flow (25 MFR) resin provides good processability with added mold release. Targeted for potential paint elimination through a wide range of high gloss opaque colors. Also available in transparent or tints. SLX2291T is targeted for broad range of automotive, building and construction, electrical, consumer and electronics applications.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Colorable
Dimensional stability
High Flow
High gloss
IR Transparent
No PFAS intentionally added
Piano black
Transparent/Translucent
Weatherable/UV stable

Industry

Material previously used in

Automotive Exteriors
Automotive Interiors
Building Component
Electrical
Heavy Truck
Lighting
Mobile Phone - Computer - Tablets
Personal Recreation
Recreational/Specialty Vehicles

Applications

Possible usage of material

All-Terrain Vehicle
Antenna
Battery Pack
Circuit Protection
City
Cowl Vent Grille
Displays
Doors Hardware/Trim
Electronic Components
Enclosure/Housing/Cover
Enclosures
Energy Management
Exterior Trim
Exterior
Front Grille
Heavy Vehicles
Interior
Lawn/Garden
LED Lighting
Meter Water
Non-LED Lighting
Oil/Gas
Personal Computing
Plumbing
Power Boat
Recreational Vehicle
Small Appliance
Smart/ID Card
Spoiler
Wiring Devices
automotive grille
automotive exterior
farm equipment body panel
agricultural equipment exterior panel
agricultural equipment exterior body panel
automotive front exterior grille
automotive front grille
automotive exterior grille
automotive exterior trim

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	350	J/m	ASTM D256
Izod Impact, notched, 23°C, 2mm	665	J/m	ASTM D256
Izod Impact, notched, -30°C	107	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	71	J	ASTM D3763
*Izod Impact, unnotched 80103 +23°C*	NB	kJ/m²	ISO 180/1U
*Izod Impact, notched 80103 +23°C*	56	kJ/m²	ISO 180/1A
*Izod Impact, notched 80103 -30°C*	12	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 +23°C*	12	kJ/m²	ISO 180/1A
*Charpy 23°C, Unnotch Edgew 80103 sp=62mm*	NB	kJ/m²	ISO 179/1eU
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	65	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80103 sp=62mm*	10	kJ/m²	ISO 179/1eA
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	12	kJ/m²	ISO 179/1eA

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	2 - 4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	280 - 310	°C
Nozzle Temperature	270 - 290	°C
Front - Zone 3 Temperature	280 - 310	°C
Middle - Zone 2 Temperature	270 - 290	°C
Rear - Zone 1 Temperature	260 - 280	°C
Hopper Temperature	60 - 80	°C
Mold Temperature	80 - 110	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	63	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	65	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	6	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	>100	%	ASTM D638
Tensile Modulus, 50 mm/min	2315	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	105	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2400	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	64	MPa	ISO 527
Tensile Stress, break, 50 mm/min	61	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	6	%	ISO 527
Tensile Strain, break, 50 mm/min	>100	%	ISO 527
Tensile Modulus, 1 mm/min	2350	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	98	MPa	ISO 178
Flexural Modulus, 2 mm/min	2410	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.2	g/cm³	ISO 1183
Specific Gravity	1.2	-	ASTM D792
Melt Flow Rate, 300°C/1.2 kgf	25	g/10 min	ASTM D1238
Water Absorption, (23°C/24hrs)	0.13	%	ASTM D570
Moisture Absorption, (23°C/50% RH/24 hrs)	0.06	%	ASTM D570
Mold Shrinkage, flow, 3.2 mm	0.5 - 0.8	%	SABIC method
Melt Volume Rate, MVR at 300°C/1.2 kg	23	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Vicat Softening Temp, Rate B/50	138	°C	ASTM D1525
HDT, 1.82 MPa, 3.2mm, unannealed	123	°C	ASTM D648
CTE, -40°C to 40°C, flow	7.E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	7.E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	7.E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	7.E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	138	°C	ISO 306
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	120	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	133	°C	ISO 75/Bf

THIS SITE USES COOKIES

LNP™ ELCRES™ SLX2291T

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

Curve Data

CAE Cards

Register for High value Multi-Point Data

THIS SITE USES COOKIES

LNP™ ELCRES™ SLX2291T

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data