ELCRES XD2322 polycarbonate (PC) copolymer resin is a UV stabilized opaque grade. This resin offers UL94 V0@1.5mm flame retardancy based on non-bromine, non-chlorine FR system, excellent low temperature ductility characteristics and processability. ELCRES XD2322 resin is an excellent candidate for a wide range of applications such as electronic vehicles (EV) and 5G devices.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Hot-Wire Ignition (HWI), PLC 2 | 3 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 3 | 1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | 3 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 1 | 1.5 | mm | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A |
| Comparative Tracking Index, M | 150 | V | IEC 60112 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | ≥1.5 | mm | UL 94 |
| UL Recognized, 94-5VA Flame Class Rating | ≥3 | mm | UL 94 |
| UV-light, water exposure/immersion | F1 | - | UL 746C |
| Glow Wire Ignitability Temperature, 1.5 mm | 825 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index, 1.5 mm | 960 | °C | IEC 60695-2-12 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 780 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 652 | J/m | ASTM D256 |
| Izod Impact, notched, -40°C | 360 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 66 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*3 +23°C | 63 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 29 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 48 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 295 - 315 | °C | |
| Nozzle Temperature | 290 - 310 | °C | |
| Front - Zone 3 Temperature | 295 - 315 | °C | |
| Middle - Zone 2 Temperature | 280 - 305 | °C | |
| Rear - Zone 1 Temperature | 270 - 295 | °C | |
| Mold Temperature | 70 - 95 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Shot to Cylinder Size | 40 - 60 | % | |
| Vent Depth | 0.025 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 58 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 59 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 112 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 2100 | MPa | ASTM D638 |
| Flexural Strength, 1.3 mm/min, 50 mm span | 92 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2400 | MPa | ASTM D790 |
| Tensile Stress, yield, 50 mm/min | 56 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 57 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 108 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2000 | MPa | ISO 527 |
| Flexural Strength, 2 mm/min | 87 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2100 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.19 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.8 | % | SABIC method |
| Mold Shrinkage, xflow, 3.2 mm | 0.4 - 0.8 | % | SABIC method |
| Melt Flow Rate, 300°C/1.2 kgf | 16 | g/10 min | ASTM D1238 |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.4 | % | ISO 62-1 |
| Moisture Absorption, (23°C/50% RH/Equilibrium) | 0.15 | % | ISO 62-4 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 15 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Relative Temp Index, Elec | 125 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 115 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 125 | °C | UL 746B |
| Vicat Softening Temp, Rate B/50 | 140 | °C | ASTM D1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 123 | °C | ASTM D648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 118 | °C | ISO 75/Af |
| CTE, -40°C to 40°C, flow | 6.1E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 6.2E-05 | 1/°C | ASTM E831 |