LNP™ ELCRIN™ 610001UiQ2

Sustainable Grade

LNP ELCRIN 610001UiQ2 (also known as ELCRIN ER011568) is a non-brominated, non-chlorinated flame retardant Polycarbonate / Polybutylene Terephthalate (PC/PBT) alloy, utilizing iQ PBT generation 2 technology with minimum 12% post consumer recycled content. Added features of this material include: good impact strength, good chemical resistance, improved heat resistance, bright white color achievable, UL V-0 rating at 1.5 mm thickness and easy flow ability.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate + PBT (PC+PBT)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Chemical Resistance
Good Processability
Heat Stabilized
High Flow
Impact resistant
Non Cl/Br flame retardant
Sustainable (Advanced Recycling)
Weatherable/UV stable

Industry

Material previously used in

Automotive Crash and Chassis
Automotive Exteriors
Automotive Interiors
Building Component
Material Handling
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Electrical Components & Infrastructure
Electrical
Electronic Components
Electronics
Enclosure/Housing/Cover
Enclosures
Exterior
Interior
Lawn/Garden
Personal Computing
Spoiler
Thermoplastic

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	1.5	mm	UL 94
UL Recognized, 94V-1 Flame Class Rating	≥0.8	mm	UL 94
UL Recognized, 94HB Flame Class Rating	≥0.4	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	800	J/m	ASTM D256
Izod Impact, notched, 0°C	700	J/m	ASTM D256
Izod Impact, notched, -30°C	342	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	60	J	ASTM D3763
Instrumented Dart Impact Energy @ peak, 23°C	50	J	ASTM D3763
Instrumented Dart Impact Peak Force, 23°C	4500	N	ASTM D3763
*Izod Impact, notched 80104 +23°C*	58	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 0°C*	44	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	17	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	60	kJ/m²	ISO 179/1eA
*Charpy 0°C, V-notch Edgew 80104 sp=62mm*	48	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	18	kJ/m²	ISO 179/1eA

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80 - 90	°C
Drying Time	3 - 4	Hrs
Drying Time (Cumulative)	8	Hrs
Maximum Moisture Content	0.04	%
Melt Temperature	245 - 275	°C
Nozzle Temperature	245 - 275	°C
Front - Zone 3 Temperature	245 - 275	°C
Middle - Zone 2 Temperature	220 - 265	°C
Rear - Zone 1 Temperature	220 - 255	°C
Mold Temperature	60 - 80	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	30 - 80	%
Vent Depth	0.038 - 0.076	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	55	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	54	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	120	%	ASTM D638
Tensile Modulus, 50 mm/min	2170	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	85	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2260	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	55	MPa	ISO 527
Tensile Stress, break, 50 mm/min	46	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5	%	ISO 527
Tensile Strain, break, 50 mm/min	105	%	ISO 527
Tensile Modulus, 1 mm/min	2120	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	83	MPa	ISO 178
Flexural Modulus, 2 mm/min	2230	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.25	-	ASTM D792
Melt Flow Rate, 265°C/5.0 kgf	23	g/10 min	ASTM D1238
Density	1.25	g/cm³	ISO 1183
Melt Volume Rate, MVR at 265°C/5.0 kg	20	cm³/10 min	ISO 1133
Moisture Absorption, (23°C/50% RH/24hrs)	0.06	%	ISO 62-4
Water Absorption, (23°C/24hrs)	0.11	%	ISO 62-1
Mold Shrinkage, flow	0.6 - 0.8	%	SABIC method
Mold Shrinkage, xflow	0.6 - 0.8	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	85	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	105	°C	ASTM D648
Vicat Softening Temp, Rate B/50	114	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	115	°C	ASTM D1525
CTE, -40°C to 40°C, flow	7.1E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	7.6E-05	1/°C	ASTM E831
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	90	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	105	°C	ISO 75/Bf

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES