Sustainable Grade
LNP ELCRIN 61000EUIG compound is based on Polycarbonate / Polybutylene Terephthalate (PC/PBT) alloy. Added features of this grade include: Impact Modified, Improved Retention of Mechanical Properties under UV Exposure and Excellent Low Temperature Impact and Chemical Resistance, that also incorporates renewable feedstock through ISCC+ mass-balance certification.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index (UL) {PLC} | 1 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 3 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥1.5 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 0 | PLC Code | UL 746A |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
| UV-light, water exposure/immersion | F2 | - | UL 746C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 710 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 530 | J/m | ASTM D256 |
| Izod Impact, notched, -40°C | 299 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 60 | J | ASTM D3763 |
| Izod Impact, notched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 30 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 55 | kJ/m² | ISO 179/1eA |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 260 - 275 | °C | |
| Nozzle Temperature | 255 - 270 | °C | |
| Front - Zone 3 Temperature | 255 - 275 | °C | |
| Middle - Zone 2 Temperature | 250 - 270 | °C | |
| Rear - Zone 1 Temperature | 245 - 265 | °C | |
| Mold Temperature | 65 - 90 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 50 - 80 | rpm | |
| Shot to Cylinder Size | 50 - 80 | % | |
| Vent Depth | 0.013 - 0.02 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 53 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 51 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 120 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2250 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 84 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2030 | MPa | ASTM D790 |
| Tensile Stress, yield, 50 mm/min | 50 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 50 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 120 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2050 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2000 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.21 | - | ASTM D792 |
| Specific Volume | 0.83 | cm³/g | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.8 - 1 | % | SABIC method |
| Mold Shrinkage on Tensile Bar, xflow | 0.8 - 1 | % | SABIC method |
| Density | 1.22 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.5 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Melt Flow Rate, 250°C/5.0 kg | 16 | g/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 15 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/50 | 122 | °C | ASTM D1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 84 | °C | ASTM D648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 107 | °C | ASTM D648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 99 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 9.5E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 9.5E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 9.5E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 9.5E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 120 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 125 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 75 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 75 | °C | UL 746B |