LNP™ ELCRIN™ 61000PUiQ2

Sustainable Grade

LNP ELCRIN 61000PUiQ2 (also known as ELCRIN ER011364) is based on Polycarbonate / Polybutylene Terephthalate (PC/PBT) alloy, utilizing iQ PBT generation 2 technology with 22% post consumer recycled content. Added features of this material include: excellent low temperature impact strength, improve retention of mechanical properties under UV exposure, good surface aesthetics, good chemical resistance and easy flow ability.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate + PBT (PC+PBT)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Aesthetics/Visual effects
Chemical Resistance
High Flow
Impact resistant
Low temperature impact
No PFAS intentionally added
Sustainable (Advanced Recycling)
Weatherable/UV stable

Industry

Material previously used in

Automotive Crash and Chassis
Automotive Exteriors
Automotive Interiors
Building Component
Commercial Appliance
Mobile Phone - Computer - Tablets
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Exterior
Interior
Lawn/Garden
Personal Computing
Spoiler

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Comparative Tracking Index (UL) {PLC}	1	PLC Code	UL 746A
Arc Resistance, Tungsten {PLC}	5	PLC Code	ASTM D495
High Voltage Arc Track Rate {PLC}	0	PLC Code	UL 746A
Hot-Wire Ignition (HWI), PLC 3	≥1.5	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 0	≥1.5	mm	UL 746A

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94HB Flame Class Rating	≥1.5	mm	UL 94
UV-light, water exposure/immersion	F2	-	UL 746C

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	560	J/m	ASTM D256
Izod Impact, notched, 0°C	530	J/m	ASTM D256
Izod Impact, notched, -40°C	240	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	54	J	ASTM D3763
Instrumented Dart Impact Energy @ peak, 23°C	49	J	ASTM D3763
Instrumented Dart Impact Peak Force, 23°C	5000	N	ASTM D3763
*Izod Impact, notched 80104 +23°C*	41	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 0°C*	40	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -40°C*	17	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	43	kJ/m²	ISO 179/1eA
*Charpy 0°C, V-notch Edgew 80104 sp=62mm*	40	kJ/m²	ISO 179/1eA
*Charpy -40°C, V-notch Edgew 80104 sp=62mm*	16	kJ/m²	ISO 179/1eA

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110	°C
Drying Time	4 - 6	Hrs
Drying Time (Cumulative)	8	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	235 - 265	°C
Nozzle Temperature	235 - 265	°C
Front - Zone 3 Temperature	235 - 265	°C
Middle - Zone 2 Temperature	235 - 265	°C
Rear - Zone 1 Temperature	235 - 265	°C
Mold Temperature	40 - 65	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	50 - 80	rpm
Shot to Cylinder Size	50 - 80	%
Vent Depth	0.013 - 0.02	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	50	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	40	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	115	%	ASTM D638
Tensile Modulus, 50 mm/min	2020	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	80	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2070	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	52	MPa	ISO 527
Tensile Stress, break, 50 mm/min	45	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5	%	ISO 527
Tensile Strain, break, 50 mm/min	159	%	ISO 527
Tensile Modulus, 1 mm/min	2040	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	78	MPa	ISO 178
Flexural Modulus, 2 mm/min	2125	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.24	-	ASTM D792
Melt Flow Rate, 250°C/5.0 kgf	46	g/10 min	ASTM D1238
Density	1.24	g/cm³	ISO 1183
Moisture Absorption, (23°C/50% RH/24hrs)	0.07	%	ISO 62-4
Water Absorption, (23°C/24hrs)	0.12	%	ISO 62-1
Melt Volume Rate, MVR at 250°C/5.0 kg	42	cm³/10 min	ISO 1133
Mold Shrinkage, flow	0.9	%	SABIC method
Mold Shrinkage, xflow	0.9	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	80	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	101	°C	ASTM D648
Vicat Softening Temp, Rate B/50	113	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	117	°C	ASTM D1525
CTE, -40°C to 40°C, flow	8.6E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	8.8E-05	1/°C	ASTM E831
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	73	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	98	°C	ISO 75/Bf
Relative Temp Index, Elec	75	°C	UL 746B
Relative Temp Index, Mech w/impact	75	°C	UL 746B
Relative Temp Index, Mech w/o impact	75	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES