Sustainable Grade
LNP ELCRIN 6F006IiQ (Formerly known under the experimental grade name ER009957), utilizing ELCRIN iQ upcycling technology, is 30% glass-reinforced, impact modified thermoplastic alloy PC/iQ PBT based compound. The grade contains a minimum of 23% PCR weight content, improved toughness and ductility.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Dielectric Constant, 1.1 GHz | 3.4 | - | SABIC method |
| Dissipation Factor, 1.1 GHz | 0.0168 | - | SABIC method |
| Dielectric Constant, 1.9 GHz | 3.41 | - | SABIC method |
| Dissipation Factor, 1.9 GHz | 0.016 | - | SABIC method |
| Dielectric Constant, 5 GHz | 3.45 | - | SABIC method |
| Dissipation Factor, 5 GHz | 0.138 | - | SABIC method |
| Dielectric Constant, 10 GHz | 3.48 | - | SABIC method |
| Dissipation Factor, 10 GHz | 0.0118 | - | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 750 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 140 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 100 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 6 | J | ASTM D3763 |
| Instrumented Dart Impact Total Energy, 23°C | 15 | J | ASTM D3763 |
| Izod Impact, notched 80*10*4 +23°C | 14 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 10 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 260 - 280 | °C | |
| Nozzle Temperature | 255 - 280 | °C | |
| Front - Zone 3 Temperature | 260 - 280 | °C | |
| Middle - Zone 2 Temperature | 255 - 275 | °C | |
| Rear - Zone 1 Temperature | 250 - 270 | °C | |
| Mold Temperature | 65 - 95 | °C | |
| Back Pressure | 0.3 - 0.6 | MPa | |
| Screw Speed | 50 - 80 | rpm | |
| Shot to Cylinder Size | 50 - 80 | % | |
| Vent Depth | 0.013 - 0.02 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 101 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 99 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2.7 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 7700 | MPa | ASTM D638 |
| Flexural Strength, 1.3 mm/min, 50 mm span | 150 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 6900 | MPa | ASTM D790 |
| Hardness, Rockwell R | 110 | - | ASTM D785 |
| Tensile Stress, break, 5 mm/min | 105 | MPa | ISO 527 |
| Tensile Modulus, 1 mm/min | 8000 | MPa | ISO 527 |
| Flexural Strength, 2 mm/min | 163 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 7600 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.44 | - | ASTM D792 |
| Melt Flow Rate, 250°C/5.0 kgf | 14 | g/10 min | ASTM D1238 |
| Density | 1.44 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 11 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 18 | cm³/10 min | ISO 1133 |
| Moisture Absorption, (23°C/50% RH/24hrs) | 0.07 | % | ISO 62-4 |
| Water Absorption, (23°C/24hrs) | 0.14 | % | ISO 62-1 |
| Mold Shrinkage, xflow | 0.4 - 0.7 | % | SABIC method |
| Mold Shrinkage, flow | 0.3 - 0.4 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/50 | 150 | °C | ASTM D1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 159 | °C | ASTM D648 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 201 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 2.70E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 9.00E-05 | 1/°C | ASTM E831 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 146 | °C | ISO 75/Af |
| Vicat Softening Temp, Rate B/50 | 150 | °C | ISO 306 |