LNP™ ELCRIN™ 6F006IiQ2

Sustainable Grade

LNP ELCRIN 6F006IiQ2 (also known as ER015808) utilizing ELCRIN iQ generation 2 upcycling technology, is a 30% glass reinforced, impact modified thermoplastic PC/iQ PBT based compound. The grade contains a minimum of 23% PCR by weight, improved toughness and ductility.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate + PBT (PC+PBT)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Good Processability
High Flow
High stiffness/Strength
Low Warpage
No PFAS intentionally added
Sustainable (Advanced Recycling)

Industry

Material previously used in

Commercial Appliance
Electrical
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Electronics
Thermoplastic

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Constant
– 1.1 GHz	3.5	-	SABIC method
– 2.45 GHz	3.52	-	SABIC method
– 5 GHz	3.49	-	SABIC method
– 10 GHz	3.49	-	SABIC method
Dissipation Factor
– 1.1 GHz	0.015	-	SABIC method
– 2.45 GHz	0.014	-	SABIC method
– 5 GHz	0.013	-	SABIC method
– 10 GHz	0.011	-	SABIC method

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94HB Flame Class Rating	≥1.5	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	15	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	9	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	50	kJ/m²	ISO 180/1U
Izod Impact, notched, 23°C	140	J/m	ASTM D256
Izod Impact, notched, -30°C	90	J/m	ASTM D256
Izod Impact, unnotched, 23°C	775	J/m	ASTM D4812
Instrumented Dart Impact Total Energy, 23°C	20	J	ASTM D3763
Instrumented Dart Impact Energy @ peak, 23°C	9	J	ASTM D3763
Instrumented Dart Impact Peak Force, 23°C	1350	N	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110	°C
Drying Time	4 - 6	Hrs
Drying Time (Cumulative)	8	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	260 - 280	°C
Rear - Zone 1 Temperature	250 - 270	°C
Middle - Zone 2 Temperature	255 - 275	°C
Front - Zone 3 Temperature	260 - 280	°C
Nozzle Temperature	255 - 280	°C
Mold Temperature	65 - 95	°C
Back Pressure	0.3 - 0.6	MPa
Screw Speed	50 - 80	rpm
Vent Depth	0.013 - 0.02	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 1 mm/min	8120	MPa	ISO 527
Tensile Stress, yield, 5 mm/min	100	MPa	ISO 527
Tensile Stress, break, 5 mm/min	100	MPa	ISO 527
Tensile Strain, break, 5 mm/min	3	%	ISO 527
Flexural Modulus, 2 mm/min	7680	MPa	ISO 178
Flexural Stress, break, 2 mm/min	155	MPa	ISO 178
Tensile Modulus, 5 mm/min	8070	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	95	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	3	%	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	7515	MPa	ASTM D790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	155	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.49	g/cm³	ISO 1183
Moisture Absorption, (23°C/50% RH/24hrs)	0.04	%	ISO 62-4
Water Absorption, (23°C/saturated)	0.09	%	ISO 62-1
Melt Volume Rate, MVR at 250°C/5 kg	9	cm³/10 min	ASTM D1238
Melt Volume Rate, MVR at 265°C/5.0 kg	18	cm³/10 min	ISO 1133
Specific Gravity	1.49	-	ASTM D792
Melt Flow Rate, 250°C/5.0 kgf	12	g/10 min	ASTM D1238
Mold Shrinkage, flow	0.3 - 0.4	%	SABIC method
Mold Shrinkage, xflow	0.4 - 0.7	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	172	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	213	°C	ISO 75/Bf
HDT, 1.82 MPa, 3.2mm, unannealed	170	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	215	°C	ASTM D648
Vicat Softening Temp, Rate B/50	165	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	165	°C	ASTM D1525
CTE, -40°C to 40°C, flow	2.0E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	1.3E-04	1/°C	ASTM E831

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience