Sustainable Grade
LNP ELCRIN 6K002XiQ compound is based on Polycarbonate / Polybutylene Terephthalate (PC/PBT) blend, utilizing ELCRIN iQ upcycling technology containing minimum 18% Post-Consumer Recycling (PCR) weight content and minerals. Added features of this grade include: good balance of Impact, Ductility and Excellent Pull-Strength.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 250 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 90 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 65 | J | ASTM D3763 |
| Izod Impact, notched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 23 | kJ/m² | ISO 179/1eA |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 255 - 275 | °C | |
| Nozzle Temperature | 250 - 265 | °C | |
| Front - Zone 3 Temperature | 250 - 270 | °C | |
| Middle - Zone 2 Temperature | 245 - 265 | °C | |
| Rear - Zone 1 Temperature | 240 - 260 | °C | |
| Mold Temperature | 40 - 90 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 80 | rpm | |
| Shot to Cylinder Size | 50 - 80 | % | |
| Vent Depth | 0.013 - 0.02 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 59 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 60 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3.9 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 130 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 4000 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 104 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3500 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 58 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 54 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3.8 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 120 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3800 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 96 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3450 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.3 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.7 - 0.9 | % | SABIC method |
| Melt Flow Rate, 250°C/5.0 kgf | 7 | g/10 min | ASTM D1238 |
| Density | 1.3 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.28 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 13 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 98 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 4.6E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 6.3E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 4.6E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 6.3E-05 | 1/°C | ISO 11359-2 |