LNP™ ELCRIN™ 6X3UiQ2G

Sustainable Grade

LNP ELCRIN 6X3UiQ2G compound is based on Polycarbonate/ Polybutylene (PC/PBT) alloy, utilizing iQ PBT generation 2 technology with minimum 12% post-consumer recycled content. It contains non-chlorinated flame retardant and is UL recognized, 94HB flame class rating at >=0.4mm. Added features of this material include good impact strength, good chemical resistance, improved heat resistance, bring white color achievable and easy flowability, that also incorporates renewable feedstock through ISCC+ mass-balance certification.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate + PBT (PC+PBT)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Chemical Resistance
Good Processability
Heat Stabilized
High Flow
Impact resistant
No PFAS intentionally added
Sustainable (Advanced Recycling)
Sustainable (bio-based offerings)
Weatherable/UV stable

Industry

Material previously used in

Automotive Crash and Chassis
Automotive Exteriors
Automotive Interiors
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Enclosure/Housing/Cover

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94HB Flame Class Rating	≥0.4	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	50	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 0°C*	45	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	19	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	58	kJ/m²	ISO 179/1eA
*Charpy 0°C, V-notch Edgew 80104 sp=62mm*	50	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	18	kJ/m²	ISO 179/1eA
Izod Impact, notched, 23°C	830	J/m	ASTM D256
Izod Impact, notched, 0°C	700	J/m	ASTM D256
Izod Impact, notched, -30°C	585	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	64	J	ASTM D3763
Instrumented Dart Impact Energy @ peak, 23°C	56	J	ASTM D3763
Instrumented Dart Impact Peak Force, 23°C	4800	N	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80 - 90	°C
Drying Time	3 - 4	Hrs
Drying Time (Cumulative)	8	Hrs
Maximum Moisture Content	0.04	%
Melt Temperature	245 - 275	°C
Rear - Zone 1 Temperature	220 - 255	°C
Middle - Zone 2 Temperature	220 - 265	°C
Front - Zone 3 Temperature	245 - 275	°C
Nozzle Temperature	245 - 275	°C
Mold Temperature	60 - 80	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	50 - 80	%
Vent Depth	0.013 - 0.02	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield, 50 mm/min	54	MPa	ISO 527
Tensile Stress, break, 50 mm/min	43	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	4	%	ISO 527
Tensile Strain, break, 50 mm/min	34	%	ISO 527
Flexural Modulus, 2 mm/min	2260	MPa	ISO 178
Flexural Stress, yield, 2 mm/min	82	MPa	ISO 178
Tensile Modulus, 50 mm/min	2190	MPa	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	116	%	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	4	%	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	57	MPa	ASTM D638
Tensile Stress, yld, Type I, 50 mm/min	56	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	2260	MPa	ASTM D790
Flexural Stress, yld, 1.3 mm/min, 50 mm span	87	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.24	g/cm³	ISO 1183
Mold Shrinkage, flow	0.6 - 0.8	%	SABIC method
Mold Shrinkage, xflow	0.6 - 0.8	%	SABIC method
Specific Gravity	1.23	-	ASTM D792
Moisture Absorption, (50% RH, Equilibrium)	0.06	%	ASTM D570
Water Absorption, (23°C/24hrs)	0.11	%	ASTM D570
Melt Volume Rate
– 265°C/5.0 kg	25	cm³/10 min	ASTM D1238

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	83	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	99	°C	ISO 75/Bf
HDT, 1.82 MPa, 3.2mm, unannealed	85	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	100	°C	ASTM D648
Vicat Softening Temp, Rate B/50	109	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	110	°C	ASTM D1525
CTE, -40°C to 40°C, flow	6.80E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	7.50E-05	1/°C	ASTM E831

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES