LNP™ ELCRIN™ 6XEUIQ2RCC

Sustainable Grade

LNP ELCRIN 6XEUIQ2RCC (also known as ELCRIN ER011567) is based on Polycarbonate / Polybutylene Terephthalate (PC/PBT) alloy, utilizing iQ PBT generation 2 technology with minimum 42% post-consumer recycle (PCR) content. Added features of this material include: excellent low temperature impact strength, good surface aesthetics, good chemical resistance.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate + PBT (PC+PBT)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Aesthetics/Visual effects
Chemical Resistance
High Flow
Impact resistant
Low temperature impact
No PFAS intentionally added
Sustainable (Advanced Recycling)
Weatherable/UV stable

Industry

Material previously used in

Automotive Crash and Chassis
Automotive Exteriors
Automotive Interiors
Building Component
Commercial Appliance
Mobile Phone - Computer - Tablets
Personal Accessory
Personal Recreation
Sport/Leisure

Applications

Possible usage of material

Bumper
Exterior
Interior
Lawn/Garden
Personal Computing
Small Appliance
Watch/Jewelry

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	50	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 0°C*	50	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -40°C*	23	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	56	kJ/m²	ISO 179/1eA
*Charpy 0°C, V-notch Edgew 80104 sp=62mm*	53	kJ/m²	ISO 179/1eA
*Charpy -40°C, V-notch Edgew 80104 sp=62mm*	21	kJ/m²	ISO 179/1eA
Izod Impact, notched, 23°C	658	J/m	ASTM D256
Izod Impact, notched, 0°C	639	J/m	ASTM D256
Izod Impact, notched, -40°C	278	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	60	J	ASTM D3763
Instrumented Dart Impact Energy @ peak, 23°C	52	J	ASTM D3763
Instrumented Dart Impact Peak Force, 23°C	4850	N	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110	°C
Drying Time	4 - 6	Hrs
Drying Time (Cumulative)	8	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	245 - 270	°C
Nozzle Temperature	245 - 270	°C
Front - Zone 3 Temperature	245 - 270	°C
Middle - Zone 2 Temperature	245 - 270	°C
Rear - Zone 1 Temperature	245 - 270	°C
Mold Temperature	65 - 90	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	50 - 80	rpm
Shot to Cylinder Size	50 - 80	%
Vent Depth	0.013 - 0.02	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	55	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5	%	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	58	MPa	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	145	%	ASTM D638
Tensile Modulus, 50 mm/min	2071	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	85	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2080	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	54	MPa	ISO 527
Tensile Strain, break, 50 mm/min	139	%	ISO 527
Tensile Stress, break, 50 mm/min	52	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	4	%	ISO 527
Flexural Modulus, 2 mm/min	2108	MPa	ISO 178
Flexural Stress, yield, 2 mm/min	81	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.2	-	ASTM D792
Density	1.2	g/cm³	ISO 1183
Melt Flow Rate, 250°C/5.0 kgf	16	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 250°C/5 kg	15	cm³/10 min	ASTM D1238
Moisture Absorption, (23°C/50% RH/24 hrs)	0.06	%	ASTM D570
Water Absorption, (23°C/24hrs)	0.11	%	ASTM D570
Mold Shrinkage, flow	0.8	%	SABIC method
Mold Shrinkage, xflow	0.8	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Melting Temperature	217	°C	ISO 11357-3
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	79	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	101	°C	ISO 75/Bf
HDT, 1.82 MPa, 3.2mm, unannealed	82	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	103	°C	ASTM D648
Vicat Softening Temp, Rate B/50	115	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	116	°C	ASTM D1525
CTE, -40°C to 40°C, flow	8.40E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	8.70E-05	1/°C	ASTM E831

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES