FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Recognized, 94HB Flame Class Rating | ≥0.75 | mm | UL 94 |
UL Yellow Card Link | View | - | - |
LNP ELCRIN CRX1314BT is an amorphous PC copolymer resin that incorporates renewable feedstock through ISCC+ mass-balance certification to lower carbon footprint without compromising product performance. Features excellent chemical resistance in combination with excellent impact strength and good optical properties (thin wall transparency). This medium flow resin features transparency to translucency based on thickness and low temperature ductility (-30C). It is intended for a wide variety of transparent and translucent healthcare applications that require improved chemical resistance and ductility.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Recognized, 94HB Flame Class Rating | ≥0.75 | mm | UL 94 |
UL Yellow Card Link | View | - | - |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 910 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 700 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 12 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 290 - 340 | °C | |
Rear - Zone 1 Temperature | 270 - 320 | °C | |
Middle - Zone 2 Temperature | 280 - 330 | °C | |
Front - Zone 3 Temperature | 290 - 340 | °C | |
Nozzle Temperature | 290 - 340 | °C | |
Mold Temperature | 80 - 105 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 50 - 100 | rpm | |
Shot to Cylinder Size | 40 - 80 | % | |
Vent Depth | 0.025 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Modulus, 50 mm/min | 2150 | MPa | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 124 | % | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 6.5 | % | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 65 | MPa | ASTM D638 |
Tensile Stress, yld, Type I, 50 mm/min | 59 | MPa | ASTM D638 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2250 | MPa | ASTM D790 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 98 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Light Transmission, 1.0 mm | 89 | % | ASTM D1003 |
Haze, 1.0 mm | 2 | % | ASTM D1003 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.19 | g/cm³ | ISO 1183 |
Moisture Absorption (23°C / 50% RH) | 0.1 | % | ISO 62 |
Water Absorption, (23°C/24hrs) | 0.2 | % | ISO 62-1 |
Melt Volume Rate, MVR at 300°C/2.16 kg | 10 | cm³/10 min | ASTM D1238 |
Specific Gravity | 1.19 | - | ASTM D792 |
Mold Shrinkage, flow | 0.5 - 0.9 | % | SABIC method |
Melt Flow Rate, 300°C/2.16 kgf | 11 | g/10 min | ASTM D1238 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 129 | °C | ASTM D648 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 142 | °C | ASTM D648 |
Vicat Softening Temp, Rate B/120 | 148 | °C | ISO 306 |