LNP™ ELCRIN™ D1000ERCC

Sustainable Grade

ELCRIN D1000ERCC is based on recycled polycarbonate (PC). Additional features of this grade include: Transparent. Good Processability. Good Ductility. Post-Consumer Recycling (PCR) polycarbonate content up to 100%.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Amorphous
Good Processability
Impact resistant
Sustainable (Mechanical Recycling)
Transparent/Translucent

Industry

Material previously used in

Consumer Goods
Home Appliances
Industrial General
Mobile Phone - Computer - Tablets
Printer Copier

Applications

Possible usage of material

Mobile Phone
Electronics
Photo/Video Camera
Thermoplastic
Wearables
printer

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80103 +23°C*	64	kJ/m²	ISO 180/1A
*Izod Impact, notched 80103 -30°C*	13	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80103 +23°C*	182	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80103 -30°C*	207	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	67	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80103 sp=62mm*	10	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80103 sp=62mm*	246	kJ/m²	ISO 179/1eU
Izod Impact, notched, 23°C	715	J/m	ASTM D256
Izod Impact, notched, -30°C	111	J/m	ASTM D256
Izod Impact, unnotched, 23°C	NB	J/m	ASTM D4812
Izod Impact, unnotched, -30°C	NB	J/m	ASTM D4812
Instrumented Dart Impact Total Energy, 23°C	53	J	ASTM D3763
Instrumented Dart Impact Ductility, 23°C	100	%	ASTM D3763

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield, 50 mm/min	63	MPa	ISO 527
Tensile Stress, break, 50 mm/min	64	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	6	%	ISO 527
Tensile Strain, break, 50 mm/min	>80	%	ISO 527
Tensile Modulus, 1 mm/min	2270	MPa	ISO 527
Flexural Modulus, 2 mm/min	2411	MPa	ISO 178
Flexural Stress, yield, 2 mm/min	110	MPa	ISO 178
Tensile Modulus, 50 mm/min	2320	MPa	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	>80	%	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	6	%	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	64	MPa	ASTM D638
Tensile Stress, yld, Type I, 50 mm/min	63	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	2440	MPa	ASTM D790
Flexural Stress, yld, 1.3 mm/min, 50 mm span	107	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.2	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.06	%	ISO 62
Mold shrinkage, flow (mold temp=100°C)	0.4 - 0.8	%	SABIC method
Mold Shrinkage, xflow	0.4 - 0.8	%	SABIC method
Melt Volume Rate, MVR at 300°C/1.2 kg	16	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 300°C/1.2 kg	16	cm³/10 min	ASTM D1238
Specific Gravity	1.2	-	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.06	%	ASTM D570
Water Absorption, (23°C/24hrs)	0.14	%	ASTM D570
Melt Flow Rate, 300°C/1.2 kgf	17	g/10 min	ASTM D1238

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	125	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	139	°C	ISO 75/Bf
HDT, 1.82 MPa, 3.2mm, unannealed	125	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	138	°C	ASTM D648
Vicat Softening Temp, Rate B/50	143	°C	ISO 306
Vicat Softening Temp, Rate B/120	146	°C	ISO 306
Vicat Softening Temp, Rate B/50	144	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	146	°C	ASTM D1525
CTE, -40°C to 40°C, flow	6.81E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	7.16E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	6.81E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	7.16E-05	1/°C	ISO 11359-2

Register for High value Multi-Point Data