LNP™ ELCRIN™ D353RCC

LNP ELCRIN D353RCC compound is based on recycled Polycarbonate (PC) resin containing 30% glass fiber. Added features of this grade include: Low Warpage, Good Ductility, Good Processability, Non-Brominated & Non-Chlorinated Flame Retardant without intentionally added PFAS. Post-Consumer Recycling (PCR) Polycarbonate content up to 40%. UL94 V2 at 0.3 mm and V0 at 1.5 mm in black only.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Industry

Material previously used in

Electrical
Electronic Components
Industrial General
Mobile Phone - Computer - Tablets
Speaker - Earphone
Wireless Communication

Applications

Possible usage of material

Electronics
EV Infrastructure
Game Player
Personal Computing
Photo/Video Camera
Small Appliance
Thin wall packaging
Structural
electrical component

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Recognized, 94V-2 Flame Class Rating	0.3	mm	UL 94
UL Recognized, 94V-0 Flame Class Rating	1.5	mm	UL 94
UL Yellow Card Link	View	-	-

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	18.5	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	51.4	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	19.1	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	58.3	kJ/m²	ISO 179/1eU
Izod Impact, notched, 23°C	160	J/m	ASTM D256
Izod Impact, unnotched, 23°C	640	J/m	ASTM D4812

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110 - 120	°C
Drying Time	4 - 6	Hrs
Melt Temperature	285 - 310	°C
Rear - Zone 1 Temperature	260 - 280	°C
Middle - Zone 2 Temperature	270 - 290	°C
Front - Zone 3 Temperature	280 - 300	°C
Nozzle Temperature	285 - 305	°C
Mold Temperature	80 - 110	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break, 5 mm/min	124	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.3	%	ISO 527
Tensile Modulus, 1 mm/min	8600	MPa	ISO 527
Flexural Modulus, 2 mm/min	8600	MPa	ISO 178
Flexural Stress, break, 2 mm/min	189	MPa	ISO 178
Tensile Modulus, 5 mm/min	8800	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.5	%	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	124	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	8300	MPa	ASTM D790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	190	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Mold Shrinkage, flow	0.1 - 0.3	%	SABIC method
Mold Shrinkage, xflow	0.1 - 0.3	%	SABIC method
Melt Volume Rate, MVR at 300°C/1.2 kg	14	cm³/10 min	ISO 1133
Specific Gravity	1.423	-	ASTM D792

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	115	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	120	°C	ISO 75/Bf
HDT, 1.82 MPa, 3.2mm, unannealed	115	°C	ASTM D648
Vicat Softening Temp, Rate B/120	125	°C	ISO 306
CTE, 0°C to 100°C, flow	2.2E-05	1/°C	ASTM E831
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES