LNP™ ELCRIN™ DC0051RC1

Sustainable Grade

LNP ELCRIN COMPOUND DC0051RC1 (experimental grade name as ER017296) is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this grade include: Flame Retardant, >75% PCR content.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Carbon fiber filled
Dimensional stability
High stiffness/Strength
Non Cl/Br flame retardant
Sustainable (Mechanical Recycling)

Industry

Material previously used in

Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Personal Computing
Mobile Phone

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.0E+06 - 1.0E+07	Ω	ASTM D257
Volume Resistivity	1.0E+07 - 1.0E+08	Ω.cm	ASTM D257

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	≥0.8	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	50	J/m	ASTM D256
Izod Impact, notched, -30°C	43	J/m	ASTM D256
Izod Impact, unnotched, 23°C	350	J/m	ASTM D4812
Izod Impact, unnotched, -30°C	325	J/m	ASTM D4812
*Izod Impact, notched 80103 +23°C*	5.9	kJ/m²	ISO 180/1A
*Izod Impact, notched 80103 -30°C*	5.1	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80103 +23°C*	23	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80103 -30°C*	26	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	6.1	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	5.3	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	27	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	29	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	5.6	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80103 sp=62mm*	4.7	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80103 sp=62mm*	24	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80103 sp=62mm*	25	kJ/m²	ISO 179/1eU
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	5.9	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	5	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	29	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80104 sp=62mm*	30	kJ/m²	ISO 179/1eU
Instrumented Dart Impact Total Energy, 23°C	13	J	ASTM D3763
Instrumented Dart Impact Energy @ peak, 23°C	10	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	70 - 80	°C
Drying Time	3 - 5	Hrs
Drying Time (Cumulative)	12	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	275 - 330	°C
Nozzle Temperature	280 - 320	°C
Front - Zone 3 Temperature	280 - 320	°C
Middle - Zone 2 Temperature	270 - 310	°C
Rear - Zone 1 Temperature	260 - 300	°C
Mold Temperature	60 - 85	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	165	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	1.8	%	ASTM D638
Tensile Modulus, 5 mm/min	17500	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	231	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	16800	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	163	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.7	%	ISO 527
Tensile Modulus, 1 mm/min	18000	MPa	ISO 527
Flexural Strength, 2 mm/min	218	MPa	ISO 178
Flexural Modulus, 2 mm/min	16500	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.31	g/cm³	ASTM D792
Melt Volume Rate, MVR at 300°C/1.2 kg	20	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 300°C/2.16 kg	41	cm³/10 min	ISO 1133
Water Absorption, (23°C/24hrs)	0.09	%	ISO 62-1
Moisture Absorption, (23°C/50% RH/24hrs)	0.03	%	ISO 62-4
Mold Shrinkage, flow	0.2 - 0.3	%	SABIC method
Mold Shrinkage, xflow	0.4 - 0.5	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	100	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	95	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	101	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	96	°C	ISO 75/Af
CTE, -40°C to 40°C, flow	7.3E-06	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	6.2E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	7.4E-06	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	6.4E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	104	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	106	°C	ASTM D1525
Vicat Softening Temp, Rate B/50	104	°C	ISO 306
Vicat Softening Temp, Rate B/120	106	°C	ISO 306
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B

Register for High value Multi-Point Data