LNP™ ELCRIN™ DF0021RC1G

Sustainable Grade

LNP ELCRIN DF0021RC1G compound is based on recycled polycarbonate (PC) resin containing 10% pre-consumer recycled glass fiber. Added features of this grade include: high modulus, non-brominated and non-chlorinated flame retardant. Post-consumer recycled (PCR) polycarbonate content up to 50%. Total recycle content up to 60%. Available in black colors, that also incorporates renewable feedstock through ISCC+ mass-balance certification.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Flame Retardant
Sustainable (bio-based offerings)

Industry

Material previously used in

Commercial Appliance
Electrical
Home Appliances

Applications

Possible usage of material

Mobile Phone
Electrical Components & Infrastructure
Enclosure/Housing/Cover

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

Electrical properties

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Constant
– 1.1 GHz	3.04	-	SABIC method
– 2.5 GHz	3.02	-	SABIC method
– 5 GHz	3.03	-	SABIC method
– 10 GHz	3.04	-	SABIC method
Dissipation Factor
– 1.1 GHz	0.007	-	SABIC method
– 2.5 GHz	0.007	-	SABIC method
– 5 GHz	0.007	-	SABIC method
– 10 GHz	0.007	-	SABIC method

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-1 Flame Class Rating	≥0.6	mm	UL 94
UL Recognized, 94V-0 Flame Class Rating	≥0.8	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	11	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	7	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	47	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	53	kJ/m²	ISO 180/1U
Izod Impact, unnotched, 23°C	720	J/m	ASTM D4812
Izod Impact, unnotched, -30°C	820	J/m	ASTM D4812
Izod Impact, notched, 23°C	100	J/m	ASTM D256
Izod Impact, notched, -30°C	80	J/m	ASTM D256
Instrumented Impact Total Energy, 23°C	21	J	ASTM D3763
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	10	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	7	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	54	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110	°C
Drying Time	3 - 6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	285 - 310	°C
Nozzle Temperature	285 - 305	°C
Front - Zone 3 Temperature	280 - 300	°C
Middle - Zone 2 Temperature	270 - 290	°C
Rear - Zone 1 Temperature	260 - 280	°C
Mold Temperature	80 - 110	°C
Back pressure (Plastic Pressure)	0.1 - 0.3	MPa
Screw Speed	50 - 90	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield, 5 mm/min	83	MPa	ISO 527
Tensile Stress, break, 5 mm/min	79	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	3.6	%	ISO 527
Tensile Strain, break, 5 mm/min	4.3	%	ISO 527
Tensile Modulus, 1 mm/min	4000	MPa	ISO 527
Flexural Stress, break, 2 mm/min	134	MPa	ISO 178
Flexural Modulus, 2 mm/min	4000	MPa	ISO 178
Tensile Stress, yld, Type I, 5 mm/min	84	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	80	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	3.7	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	4.6	%	ASTM D638
Tensile Modulus, 5 mm/min	4000	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	137	MPa	ASTM D790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	136	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	3700	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.27	g/cm³	ISO 1183
Melt Volume Rate, MVR at 300°C/1.2 kg	11	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 300°C/2.16 kg	23	cm³/10 min	ISO 1133
Specific Gravity	1.27	-	ASTM D792
Mold Shrinkage, flow	0.3 - 0.6	%	SABIC method
Mold Shrinkage, xflow	0.3 - 0.6	%	SABIC method
Melt Flow Rate, 300°C/1.2 kgf	14	g/10 min	ASTM D1238
Melt Flow Rate, 300°C/2.16 kgf	26	g/10 min	ASTM D1238

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	121	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	115	°C	ISO 75/Af
Vicat Softening Temp, Rate B/50	123	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	126	°C	ASTM D1525
HDT, 0.45 MPa, 3.2 mm, unannealed	121	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	116	°C	ASTM D648
CTE, -40°C to 40°C, flow	3.9E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	8.0E-05	1/°C	ASTM E831

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES