LNP™ ELCRIN™ DF0023RCCG

Sustainable Grade

LNP ELCRIN DF0023RCCG compound is based on recycled Polycarbonate (PC) resin containing 10% glass fiber. Added features of this grade include: Good Ductility, Good Processability, Non-Brominated & Non-Chlorinated Flame Retardant, Light-blocking at 0.5 mm. Post-Consumer Recycling (PCR) Polycarbonate content up to 50%. UL94 V2 at 0.3 mm and V0 at 1.5 mm, that also incorporates renewable feedstock through ISCC+ mass-balance certification.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Sustainable (bio-based offerings)

Industry

Material previously used in

Electronic Components
Mobile Phone - Computer - Tablets
Speaker - Earphone

Applications

Possible usage of material

Displays
Electrical Components & Infrastructure
Electronic Components
Electronics
Enclosures
EV Infrastructure
EV/HEV Charging System
Personal Computing
Photo/Video Camera

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Recognized, 94V-2 Flame Class Rating	0.3	mm	UL 94
UL Recognized, 94V-0 Flame Class Rating	1.5	mm	UL 94
UL Yellow Card Link	View	-	-

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	17	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	110	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	18	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	123	kJ/m²	ISO 179/1eU
Izod Impact, notched, 23°C	220	J/m	ASTM D256
Izod Impact, unnotched, 23°C	1600	J/m	ASTM D4812
Instrumented Dart Impact Total Energy, 23°C	75	J	ASTM D3763
Instrumented Dart Impact Energy @ peak, 23°C	17	J	ASTM D3763
Instrumented Dart Impact Peak Force, 23°C	1.6	N	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110	°C
Drying Time	3 - 4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	285 - 310	°C
Rear - Zone 1 Temperature	260 - 280	°C
Middle - Zone 2 Temperature	270 - 290	°C
Front - Zone 3 Temperature	280 - 300	°C
Nozzle Temperature	285 - 305	°C
Mold Temperature	80 - 110	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield, 5 mm/min	52	MPa	ISO 527
Tensile Stress, break, 5 mm/min	38	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	4	%	ISO 527
Tensile Strain, break, 5 mm/min	9	%	ISO 527
Tensile Modulus, 1 mm/min	4000	MPa	ISO 527
Tensile Modulus, 5 mm/min	4000	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	10	%	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	4	%	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	39	MPa	ASTM D638
Tensile Stress, yld, Type I, 5 mm/min	52	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	3400	MPa	ASTM D790
Flexural Stress, yld, 1.3 mm/min, 50 mm span	92	MPa	ASTM D790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	91	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.27	g/cm³	ISO 1183
Mold Shrinkage, flow	0.3 - 0.5	%	SABIC method
Mold Shrinkage, xflow	0.3 - 0.5	%	SABIC method
Melt Volume Rate, MVR at 300°C/1.2 kg	10	cm³/10 min	ISO 1133
Specific Gravity	1.28	-	ASTM D792

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	113	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	118	°C	ISO 75/Bf
HDT, 1.82 MPa, 3.2mm, unannealed	115	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	121	°C	ASTM D648
Vicat Softening Temp, Rate B/120	121	°C	ISO 306
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience