LNP™ ELCRIN™ DF0033RCCG

Sustainable Grade

LNP ELCRIN DF0033RCCG compound is based on Post-Consumer Recycling (PCR) Polycarbonate resin containing glass fiber, Flame retardant. Added features of this grade include: low warpage, good ductility, good processability, lightblocking at 0.5mm, opaque black, Non-Brominated & Non-Chlorinated Flame Retardant. Post-Consumer Recycling (PCR) Polycarbonate content up to 50%, UL 94V2 at 0.6mm and V0 at 3mm in opaque black only, that also incorporates renewable feedstock through ISCC+ mass-balance certification.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Flame Retardant
Non Cl/Br flame retardant
Non halogenated flame retardant
Sustainable (bio-based offerings)

Industry

Material previously used in

Electrical
Electronic Components
Industrial General
Mobile Phone - Computer - Tablets
Speaker - Earphone
Wireless Communication

Applications

Possible usage of material

Data Management
Displays
Electrical Components & Infrastructure
Electronic Components
Electronics
Enclosures
EV Infrastructure
Game Player
Personal Computing
Photo/Video Camera
Small Appliance
Thin wall packaging
Structural

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Recognized, 94V-2 Flame Class Rating	0.6	mm	UL 94
UL Recognized, 94V-0 Flame Class Rating	3	mm	UL 94
UL Yellow Card Link	View	-	-

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	6	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	40	kJ/m²	ISO 180/1U
Izod Impact, notched, 23°C	50	J/m	ASTM D256
Izod Impact, unnotched, 23°C	600	J/m	ASTM D4812

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110 - 120	°C
Drying Time	4 - 6	Hrs
Melt Temperature	285 - 310	°C
Rear - Zone 1 Temperature	260 - 280	°C
Middle - Zone 2 Temperature	270 - 290	°C
Front - Zone 3 Temperature	280 - 300	°C
Nozzle Temperature	285 - 305	°C
Mold Temperature	80 - 110	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 5 mm/min	4700	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	3.5	%	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	2.9	%	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	80	MPa	ASTM D638
Tensile Stress, yld, Type I, 5 mm/min	75	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	4500	MPa	ASTM D790
Flexural Stress, yld, 1.3 mm/min, 50 mm span	137	MPa	ASTM D790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	124	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.31	g/cm³	ISO 1183
Mold Shrinkage, xflow, 24 hrs	0.1 - 0.3	%	ISO 294
Mold Shrinkage, flow, 24 hrs	0.2 - 0.4	%	ISO 294
Melt Volume Rate, MVR at 300°C/1.2 kg	12	cm³/10 min	ASTM D1238
Specific Gravity	1.31	-	ASTM D792

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	118	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	121	°C	ASTM D648
CTE, -30°C to 80°C, flow	3.6E-05	1/°C	ASTM E831
CTE, -30°C to 80°C, xflow	6.8E-05	1/°C	ASTM E831
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES