LNP™ ELCRIN™ DF0036RCC

Sustainable Grade

LNP ELCRIN DF0036RCC compound is based on recycled Polycarbonate (PC) resin containing 15% glass fiber. Added features of this grade include: Low Warpage, Good Ductility, Good Processability, Non-Brominated & Non-Chlorinated Flame Retardant, Light Blocking at 0.5mm, High Reflective white & opaque black. Post-Consumer Recycling (PCR) Polycarbonate content up to 50%.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Flame Retardant
Good Processability
Impact resistant
Low Warpage
Non Cl/Br flame retardant
Sustainable (Mechanical Recycling)

Industry

Material previously used in

Building Component
Electrical
Mobile Phone - Computer - Tablets
Personal Accessory

Applications

Possible usage of material

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	1.5	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	6	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	30	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	5	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	36	kJ/m²	ISO 179/1eU
Izod Impact, notched, 23°C	64	J/m	ASTM D256
Izod Impact, unnotched, 23°C	480	J/m	ASTM D4812
Instrumented Dart Impact Total Energy, 23°C	20	J	ASTM D3763
Instrumented Dart Impact Energy @ peak, 23°C	17	J	ASTM D3763
Instrumented Dart Impact Peak Force, 23°C	2500	N	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Time	110	Hrs
Drying Time	4 - 6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	285 - 310	°C
Rear - Zone 1 Temperature	260 - 280	°C
Middle - Zone 2 Temperature	270 - 290	°C
Front - Zone 3 Temperature	280 - 300	°C
Nozzle Temperature	285 - 305	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.1 - 0.3	MPa
Screw Speed	30 - 90	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 1 mm/min	4480	MPa	ISO 527
Tensile Stress, yield, 5 mm/min	73	MPa	ISO 527
Tensile Stress, break, 5 mm/min	71	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	2.5	%	ISO 527
Tensile Strain, break, 5 mm/min	2.8	%	ISO 527
Flexural Modulus, 2 mm/min	4650	MPa	ISO 178
Flexural Stress, yield, 2 mm/min	125	MPa	ISO 178
Tensile Modulus, 5 mm/min	4460	MPa	ASTM D638
Tensile Stress, yld, Type I, 5 mm/min	73	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	69	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	2.6	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	3.3	%	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	4540	MPa	ASTM D790
Flexural Stress, yld, 1.3 mm/min, 50 mm span	125	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.33	g/cm³	ISO 1183
Melt Flow Rate, 300°C/1.2 kgf	11	g/10 min	ASTM D1238
Water Absorption, (23°C/24hrs)	0.1	%	ISO 62-1
Mold Shrinkage, flow	0.1 - 0.3	%	SABIC method
Mold Shrinkage, xflow	0.2 - 0.4	%	SABIC method
Melt Volume Rate, MVR at 300°C/1.2 kg	9	cm³/10 min	ISO 1133
Specific Gravity	1.34	-	ASTM D792

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	120	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	126	°C	ISO 75/Bf
Vicat Softening Temp, Rate B/50	127	°C	ISO 306
Vicat Softening Temp, Rate B/120	129	°C	ISO 306
HDT, 1.82 MPa, 3.2mm, unannealed	120	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	125	°C	ASTM D648
Vicat Softening Temp, Rate B/50	128	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	130	°C	ASTM D1525
CTE, 23°C to 50°C, flow	3.1E-05	1/°C	ASTM E831
CTE, 23°C to 50°C, xflow	8.4E-05	1/°C	ASTM E831
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES