LNP™ ELCRIN™ DF004G

Sustainable Grade

LNP ELCRIN DF004G compound is based on Polycarbonate (PC) resin containing 20% glass fiber, that also incorporates renewable feedstock through ISCC+ mass-balance certification.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High stiffness/Strength
No PFAS intentionally added
Sustainable (bio-based offerings)

Industry

Material previously used in

Building Component
Electrical
Mobile Phone - Computer - Tablets
Personal Accessory

Applications

Possible usage of material

Displays
Document Handling
Medical Device
Traffic Management

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
High Voltage Arc Track Rate {PLC}	-	PLC Code	UL 746A
Hot-Wire Ignition (HWI), PLC 0	-	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 2	-	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 4	-	mm	UL 746A

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	-	-	-
UL Recognized, 94V-1 Flame Class Rating	-	mm	UL 94
UL Recognized, 94V-2 Flame Class Rating	-	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	-	J/m	ASTM D4812
Izod Impact, notched, 23°C	-	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	-	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	-	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	-	°C
Drying Time	-	Hrs
Maximum Moisture Content	-	%
Melt Temperature	-	°C
Front - Zone 3 Temperature	-	°C
Middle - Zone 2 Temperature	-	°C
Rear - Zone 1 Temperature	-	°C
Mold Temperature	-	°C
Back Pressure	-	MPa
Screw Speed	-	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	-	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	-	%	ASTM D638
Tensile Modulus, 50 mm/min	-	MPa	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	-	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	-	MPa	ASTM D790
Tensile Modulus, 1 mm/min	-	MPa	ISO 527

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	-	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	-	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	-	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	-	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	-	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	-	%	ISO 294
Density	-	g/cm³	ISO 1183

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	-	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	-	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	-	°C	ISO 75/Af
Relative Temp Index, Elec	-	°C	UL 746B
Relative Temp Index, Mech w/impact	-	°C	UL 746B
Relative Temp Index, Mech w/o impact	-	°C	UL 746B

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
High Voltage Arc Track Rate {PLC}	-	PLC Code	UL 746A
Hot-Wire Ignition (HWI), PLC 0	-	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 2	-	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 4	-	mm	UL 746A

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	-	-	-
UL Recognized, 94V-1 Flame Class Rating	-	mm	UL 94
UL Recognized, 94V-2 Flame Class Rating	-	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	-	J/m	ASTM D4812
Izod Impact, notched, 23°C	-	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	-	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	-	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	-	°C
Drying Time	-	Hrs
Maximum Moisture Content	-	%
Melt Temperature	-	°C
Front - Zone 3 Temperature	-	°C
Middle - Zone 2 Temperature	-	°C
Rear - Zone 1 Temperature	-	°C
Mold Temperature	-	°C
Back Pressure	-	MPa
Screw Speed	-	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break	-	MPa	ASTM D638
Tensile Strain, break	-	%	ASTM D638
Tensile Modulus, 50 mm/min	-	MPa	ASTM D638
Flexural Stress	-	MPa	ASTM D790
Flexural Modulus	-	MPa	ASTM D790
Tensile Stress, break	-	MPa	ISO 527
Tensile Strain, break	-	%	ISO 527
Tensile Modulus, 1 mm/min	-	MPa	ISO 527
Flexural Stress	-	MPa	ISO 178
Flexural Modulus	-	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	-	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	-	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	-	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	-	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	-	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	-	%	ISO 294
Density	-	g/cm³	ISO 1183

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	-	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	-	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	-	°C	ISO 75/Af
Relative Temp Index, Elec	-	°C	UL 746B
Relative Temp Index, Mech w/impact	-	°C	UL 746B
Relative Temp Index, Mech w/o impact	-	°C	UL 746B

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
High Voltage Arc Track Rate {PLC}	-	PLC Code	UL 746A
Hot-Wire Ignition (HWI), PLC 0	-	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 2	-	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 4	-	mm	UL 746A

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	-	-	-
UL Recognized, 94V-1 Flame Class Rating	-	mm	UL 94
UL Recognized, 94V-2 Flame Class Rating	-	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, unnotched 80104 +23°C*	-	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	-	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	-	°C
Drying Time	-	Hrs
Maximum Moisture Content	-	%
Melt Temperature	-	°C
Front - Zone 3 Temperature	-	°C
Middle - Zone 2 Temperature	-	°C
Rear - Zone 1 Temperature	-	°C
Mold Temperature	-	°C
Back Pressure	-	MPa
Screw Speed	-	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield, 5 mm/min	-	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	-	%	ISO 527
Tensile Modulus, 1 mm/min	-	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	-	MPa	ISO 178
Flexural Modulus, 2 mm/min	-	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	-	g/cm³	ISO 1183

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	-	°C	ISO 75/Af
Relative Temp Index, Elec	-	°C	UL 746B
Relative Temp Index, Mech w/impact	-	°C	UL 746B
Relative Temp Index, Mech w/o impact	-	°C	UL 746B

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
High Voltage Arc Track Rate {PLC}	4	PLC Code	UL 746A
Hot-Wire Ignition (HWI), PLC 0	≥1.5	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 2	≥3	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 4	≥1.5	mm	UL 746A

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-1 Flame Class Rating	≥3	mm	UL 94
UL Recognized, 94V-2 Flame Class Rating	≥1.5	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	961	J/m	ASTM D4812
Izod Impact, notched, 23°C	133	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	61	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	8	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	305 - 325	°C
Front - Zone 3 Temperature	320 - 330	°C
Middle - Zone 2 Temperature	310 - 320	°C
Rear - Zone 1 Temperature	295 - 305	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break	91	MPa	ASTM D638
Tensile Strain, break	9.5	%	ASTM D638
Tensile Modulus, 50 mm/min	5510	MPa	ASTM D638
Flexural Stress	149	MPa	ASTM D790
Flexural Modulus	5510	MPa	ASTM D790
Tensile Stress, break	102	MPa	ISO 527
Tensile Strain, break	8	%	ISO 527
Tensile Modulus, 1 mm/min	6000	MPa	ISO 527
Flexural Stress	148	MPa	ISO 178
Flexural Modulus	6000	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.35	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.1	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.2	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.5	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	0.2	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.45	%	ISO 294
Density	1.35	g/cm³	ISO 1183

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	144	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	139	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	142	°C	ISO 75/Af
Relative Temp Index, Elec	125	°C	UL 746B
Relative Temp Index, Mech w/impact	115	°C	UL 746B
Relative Temp Index, Mech w/o impact	125	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES

LNP™ ELCRIN™ DF004G

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

Related Documents

Register for High value Multi-Point Data