LNP™ ELCRIN™ DF006PRC1

LNP ELCRIN DF006PRC1 is a compound based on Recycle Polycarbonate resin containing PIR Glass Fiber. Added features of this material include: high modulus, good flatness, good ductility. Recycling content up to 50%.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High Flow
High stiffness/Strength
Impact resistant
No PFAS intentionally added

Industry

Material previously used in

Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Mobile Phone

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod impact, notched
– -20°C	140	J/m	ASTM D256
– 23°C	170	J/m	ASTM D256
– 80104 +23°C	13	kJ/m²	ISO 180/1A
Izod Impact, Unnotched
– 23°C	680	J/m	ASTM D4812
– 80104 +23°C	52	kJ/m²	ISO 180/1U

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110 - 120	°C
Drying Time	4 - 6	Hrs
Melt Temperature	285 - 310	°C
Nozzle Temperature	285 - 305	°C
Front - Zone 3 Temperature	280 - 300	°C
Middle - Zone 2 Temperature	270 - 290	°C
Rear - Zone 1 Temperature	260 - 280	°C
Mold Temperature	80 - 110	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	117	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.8	%	ASTM D638
Tensile Modulus, 5 mm/min	7380	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	184	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	7410	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	110	MPa	ISO 527
Tensile Strain, break, 5 mm/min	3	%	ISO 527
Tensile Modulus, 1 mm/min	7300	MPa	ISO 527
Flexural Strength, 2 mm/min	165	MPa	ISO 178
Flexural Modulus, 2 mm/min	6800	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.4	-	ASTM D792
Density	1.4	g/cm³	ISO 1183
Melt Volume Rate, MVR at 300°C/1.2 kg	8	cm³/10 min	ISO 1133
Mold Shrinkage, flow	0.3 - 0.5	%	SABIC method
Mold Shrinkage, xflow	0.3 - 0.5	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	131	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	132	°C	ASTM D648
HDT, 1.82 MPa, 6.4 mm, unannealed	128	°C	ASTM D648
HDT, 0.45 MPa, 6.4 mm, unannealed	130	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	128	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	130	°C	ISO 75/Bf

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES