FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 1.2 | mm | UL 94 |
LNP ELCRIN DM0051RC compound is based on Polycarbonate (PC) resin containing minerals. Added features include: High Modulus, Good Flow, Good Ductility, Low Warpage and Non-Brominated & Non-Chlorinated Flame Retardant. This product has a PCR content up to 50%
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 1.2 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 58 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 38 | J/m | ASTM D256 |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 4.6 | kJ/m² | ISO 179/1eA |
Instrumented Dart Impact Total Energy, 23°C | 15 | J | ASTM D3763 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 90 - 105 | °C | |
Drying Time | 4 - 6 | Hrs | |
Melt Temperature | 270 - 300 | °C | |
Nozzle Temperature | 280 - 300 | °C | |
Front - Zone 3 Temperature | 270 - 290 | °C | |
Middle - Zone 2 Temperature | 260 - 280 | °C | |
Rear - Zone 1 Temperature | 250 - 270 | °C | |
Mold Temperature | 70 - 90 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 5 mm/min | 59 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 38 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min | 2.8 | % | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 5.2 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 5800 | MPa | ASTM D638 |
Flexural Strength, 1.3 mm/min, 50 mm span | 98 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 5110 | MPa | ASTM D790 |
Tensile Stress, yield, 5 mm/min | 58 | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min | 35 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | 2.8 | % | ISO 527 |
Tensile Strain, break, 5 mm/min | 5 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 5750 | MPa | ISO 527 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.39 | - | ASTM D792 |
Density | 1.39 | g/cm³ | ISO 1183 |
Melt Flow Rate, 260°C/2.16 kgf | 9.5 | g/10 min | ASTM D1238 |
Mold Shrinkage, flow, 24 hrs | 0.25 | % | ISO 294 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 90 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 82 | °C | ASTM D648 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 84 | °C | ISO 75/Af |
CTE, 23°C to 80°C, flow | 3.8E-5 | 1/°C | ISO 11359-2 |
CTE, 23°C to 80°C, xflow | 7.4E-5 | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/50 | 95 | °C | ASTM D1525 |
Relative Temp Index, Elec | 80 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |