LNP™ ELCRIN™ DMX6034RCC

ELCRIN DMX6034RCC is an improved scratch resistant polycarbonate copolymer that contains 20% Post consumer recycle content. This medium flow, UV stabilized, custom colorable resin is an excellent candidate for wide variety of electronics, consumer, and industrial applications that require improved scratch resistance.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Impact resistant
No PFAS intentionally added
Scratch Resistance
Weatherable/UV stable

Industry

Material previously used in

Automotive Interiors
Commercial Appliance
Home Appliances
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Mobile Phone
Commercial Appliance
Electronic Components
Electronics
Enclosure/Housing/Cover

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80103 +23°C*	37	kJ/m²	ISO 180/1A
*Izod Impact, notched 80103 -30°C*	72	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80103 +23°C*	178	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80103 -30°C*	183	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	40	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80103 sp=62mm*	9	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80103 sp=62mm*	297	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80103 sp=62mm*	262	kJ/m²	ISO 179/1eU
Izod Impact, notched, 23°C	515	J/m	ASTM D256
Izod Impact, notched, 0°C	258	J/m	ASTM D256
Izod Impact, notched, -30°C	116	J/m	ASTM D256
Izod Impact, unnotched, 23°C	NB	J/m	ASTM D4812
Izod Impact, unnotched, -30°C	NB	J/m	ASTM D4812
Instrumented Dart Impact Total Energy, 23°C	67	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110	°C
Drying Time	3 - 4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	290 - 310	°C
Rear - Zone 1 Temperature	260 - 280	°C
Middle - Zone 2 Temperature	280 - 305	°C
Front - Zone 3 Temperature	290 - 310	°C
Nozzle Temperature	290 - 310	°C
Mold Temperature	60 - 85	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield, 50 mm/min	60	MPa	ISO 527
Tensile Stress, break, 50 mm/min	55	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	6	%	ISO 527
Tensile Strain, break, 50 mm/min	93	%	ISO 527
Tensile Modulus, 1 mm/min	2068	MPa	ISO 527
Flexural Modulus, 2 mm/min	2120	MPa	ISO 178
Flexural Stress, yield, 2 mm/min	86	MPa	ISO 178
Tensile Modulus, 50 mm/min	2190	MPa	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	75	%	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	7	%	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	59	MPa	ASTM D638
Tensile Stress, yld, Type I, 50 mm/min	61	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	2100	MPa	ASTM D790
Flexural Stress, yld, 1.3 mm/min, 50 mm span	97	MPa	ASTM D790
Pencil Hardness test, 0.5 kgf	F	-	ASTM D3363
Hardness, Rockwell M	62	-	ASTM D785

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.16	g/cm³	ISO 1183
Moisture Absorption, (23°C/50% RH/24 hrs)	0.06	%	ASTM D570
Water Absorption, (23°C/24hrs)	0.11	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.5 - 0.8	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.5 - 0.8	%	ASTM D955
Specific Gravity	1.17	-	ASTM D792
Melt Volume Rate, MVR at 300°C/1.2 kg	9	cm³/10 min	ISO 1133
Melt Flow Rate, 300°C/1.2 kgf	10	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 300°C/1.2 kg	9	cm³/10 min	ASTM D1238

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	112	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	129	°C	ISO 75/Bf
HDT, 1.82 MPa, 3.2mm, unannealed	117	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	131	°C	ASTM D648
Vicat Softening Temp, Rate B/50	136	°C	ISO 306
Vicat Softening Temp, Rate B/120	138	°C	ISO 306
Vicat Softening Temp, Rate B/50	136	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	138	°C	ASTM D1525
CTE, -40°C to 40°C, flow	7.5E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	7.7E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, flow	7.5E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	7.7E-05	1/°C	ASTM E831

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES