LNP™ ELCRIN™ DX11355RC

Sustainable Grade

LNP ELCRIN DX11355RC compound is based on recycled Polycarbonate (PC) resin containing proprietary additives and available in black color only. Added features of this grade include: Improved Plating Surface and Mechanical Performance targeted for Laser Direct Structuring (LDS) applications, Improved Impact, Non-Brominated, Non-Chlorinated Flame Retardant. Post-Consumer Recycling (PCR) Polycarbonate content up to 50%.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Dimensional stability
Impact resistant
Laser Direct Structuring
Non Cl/Br flame retardant
Sustainable (Mechanical Recycling)

Industry

Material previously used in

Commercial Appliance
Electronic Components
Mobile Phone - Computer - Tablets
Personal Accessory
Speaker - Earphone
Wireless Communication

Applications

Possible usage of material

Mobile Phone
Antenna
Electronic Components
Personal Computing
Security/Detection
Small Appliance
Wearables
Wireless Communications
mobile phone antenna
laptop antenna
wearable device antenna
lds
laser direct structuring
outdoor device antenna

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Constant, 1.1 GHz	2.89	-	SABIC method
Dissipation Factor, 1.1 GHz	0.008	-	SABIC method
Dielectric Constant, 1.9 GHz	2.92	-	SABIC method
Dissipation Factor, 1.9 GHz	0.007	-	SABIC method
Dielectric Constant, 5 GHz	2.91	-	SABIC method
Dissipation Factor, 5 GHz	0.006	-	SABIC method

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	0.7	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact
– notched, 23°C	817	J/m	ASTM D257
– unnotched, 23°C	NB	J/m	ASTM D4812
– notched 80103 +23°C	104	kJ/m²	ISO 180/1A
– unnotched 80103 +23°C	NB	kJ/m²	ISO 180/1U
– notched 80103 0°C	68	kJ/m²	ISO 180/1A
– unnotched 80103 0°C	NB	kJ/m²	ISO 180/1U
– notched 80103 -20°C	20	kJ/m²	ISO 180/1A
– unnotched 80103 -20°C	NB	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	100	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80103 sp=62mm*	NB	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 110	°C
Drying Time	3 - 4	Hrs
Drying Time (Cumulative)	8	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	280 - 315	°C
Nozzle Temperature	280 - 315	°C
Front - Zone 3 Temperature	270 - 310	°C
Middle - Zone 2 Temperature	265 - 305	°C
Rear - Zone 1 Temperature	260 - 290	°C
Mold Temperature	60 - 90	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.25 - 0.76	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	59	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	53	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	4.7	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	55	%	ASTM D638
Tensile Modulus, 50 mm/min	2680	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	91	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2480	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	58	MPa	ISO 527
Tensile Stress, break, 50 mm/min	47	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5.1	%	ISO 527
Tensile Strain, break, 50 mm/min	45	%	ISO 527
Tensile Modulus, 1 mm/min	2680	MPa	ISO 527
Flexural Strength, 2 mm/min	88	MPa	ISO 178
Flexural Modulus, 2 mm/min	2620	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.27	-	ASTM D792
Water Absorption, (23°C/24hrs)	0.11	%	ISO 62-1
Moisture Absorption, (23°C/50% RH/24hrs)	0.04	%	ISO 62-4
Melt Volume Rate, MVR at 260°C/5.0 kg	8	cm³/10 min	ISO 1133
Mold Shrinkage, flow	0.6 - 0.8	%	SABIC method
Mold Shrinkage, xflow	0.6 - 0.8	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	130	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	117	°C	ASTM D648
CTE, -40°C to 40°C, flow	6.3E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	7.0E-05	1/°C	ASTM E831
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES