LNP™ ELCRIN™ EXL9410KG

Sustainable Grade

LNP ELCRIN EXL9410KG is an opaque polycarbonate (PC) siloxane copolymer resin, that incorporates renewable feedstock through ISCC+ mass-balance certification, offers extreme low temperature (-50 C) ductility in combination with excellent processability. This medium flow resin features UL 94 V0 1.5mm rating with non-chlorinated, non-brominated flame-retardant agents for wide range of colors, and No PFAS intentionally added. EXL9410KG is an excellent candidate for a broad range of applications such as mobile phones, tablets, industrial housings, and electric vehicle supply equipment (EVSE) housings.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Amorphous
Flame Retardant
Good Processability
Impact resistant
Low temperature impact
No PFAS intentionally added
Sustainable (bio-based offerings)

Industry

Material previously used in

Consumer Goods
Electrical
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Electrical Components & Infrastructure
Electronic Components
Enclosure/Housing/Cover

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Recognized, 94V-0 Flame Class Rating	≥1.5	mm	UL 94
Glow Wire Ignitability Temperature, 3.0 mm	850	°C	IEC 60695-2-13
Glow Wire Flammability Index, 3.0 mm	960	°C	IEC 60695-2-12
UL Yellow Card Link	View	-	-

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	66	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	215	kJ/m²	ISO 180/1U
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	300	kJ/m²	ISO 179/1eU
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	70	kJ/m²	ISO 179/1eA
Izod Impact, notched, 23°C	840	J/m	ASTM D256
Izod Impact, notched, -30°C	725	J/m	ASTM D256
Izod Impact, notched, -50°C	660	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	58	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	3 - 4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	295 - 315	°C
Rear - Zone 1 Temperature	270 - 295	°C
Middle - Zone 2 Temperature	280 - 305	°C
Front - Zone 3 Temperature	290 - 315	°C
Nozzle Temperature	290 - 310	°C
Mold Temperature	70 - 110	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Strain, brk, Type I, 50 mm/min	100	%	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5	%	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	60	MPa	ASTM D638
Tensile Stress, yld, Type I, 50 mm/min	53	MPa	ASTM D638
Tensile Modulus, 50 mm/min	2030	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	2160	MPa	ASTM D790
Flexural Stress, yld, 1.3 mm/min, 50 mm span	86	MPa	ASTM D790
Tensile Modulus, 1 mm/min	2020	MPa	ISO 527
Tensile Stress, yield, 50 mm/min	54	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5	%	ISO 527
Tensile Strain, break, 50 mm/min	125	%	ISO 527
Tensile Stress, break, 50 mm/min	58	MPa	ISO 527

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Melt Volume Rate, MVR at 300°C/1.2 kg	9	cm³/10 min	ISO 1133
Specific Gravity	1.2	-	ASTM D792
Water Absorption, (23°C/Saturated)	0.13	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.4 - 0.8	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.4 - 0.8	%	ASTM D955
Melt Flow Rate, 300°C/1.2 kgf	10	g/10 min	ASTM D1238

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	110	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	123	°C	ISO 75/Bf
HDT, 1.82 MPa, 3.2mm, unannealed	110	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	123	°C	ASTM D648
Vicat Softening Temp, Rate A/50	136	°C	ASTM D1525
CTE, -40°C to 40°C, flow	6.60E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	7.00E-05	1/°C	ASTM E831
Relative Temp Index, Elec	120	°C	UL 746B
Relative Temp Index, Mech w/impact	110	°C	UL 746B
Relative Temp Index, Mech w/o impact	120	°C	UL 746B
Ball Pressure Test, approximate maximum	120	°C	IEC 60695-10-2
Vicat Softening Temp, Rate B/50	130	°C	ISO 306

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES