Sustainable Grade
LNP ELCRIN EXL9414TG resin, that incorporates renewable feedstock through ISCC+ mass-balance certification, is a halogen-free flame-retardant Polycarbonate (PC) featuring transparency, -40 degree C ductility and UL-94 V0 rating for injection molding applications. Excellent impact combined with good flow, transparent and colorability for aesthetics and thin-wall flame retardancy makes this product is intended for thin-wall applications
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 3 | ≥1 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 4 | ≥0.8 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥0.8 | mm | UL 746A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Yellow Card Link 2 | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | ≥1.8 | mm | UL 94 |
| UL Recognized, 94V-1 Flame Class Rating | ≥1.5 | mm | UL 94 |
| UL Recognized, 94V-2 Flame Class Rating | ≥1.2 | mm | UL 94 |
| UV-light, water exposure/immersion | f1 | - | UL 746C |
| Glow Wire Ignitability Temperature, 3.0 mm | 850 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 2.0 mm | 850 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 1.5 mm | 875 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 1.0 mm | 875 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 0.75 mm | 875 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 2.0 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 1.5 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 1.0 mm | 930 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 0.75 mm | 930 | °C | IEC 60695-2-12 |
| Oxygen Index (LOI) | 35 | % | ISO 4589 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 824 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 712 | J/m | ASTM D256 |
| Izod Impact, notched, -40°C | 593 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 75 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*3 +23°C | 65 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 55 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 70 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 60 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 48 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 295 - 315 | °C | |
| Nozzle Temperature | 290 - 310 | °C | |
| Front - Zone 3 Temperature | 295 - 315 | °C | |
| Middle - Zone 2 Temperature | 280 - 305 | °C | |
| Rear - Zone 1 Temperature | 270 - 295 | °C | |
| Mold Temperature | 70 - 95 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Shot to Cylinder Size | 40 - 60 | % | |
| Vent Depth | 0.025 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 57 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 59 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5.6 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 123.9 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2180 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 92 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2180 | MPa | ASTM D790 |
| Tensile Stress, yield, 50 mm/min | 56 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 55 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 5.4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 108 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2300 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 88 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2120 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Light Transmission at 2.0 mm | 84 | % | SABIC method |
| Haze, 2mm | 3 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.19 | - | ASTM D792 |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Flow Rate, 300°C/1.2 kgf | 13 | g/10 min | ASTM D1238 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 12 | cm³/10 min | ISO 1133 |
| Moisture Absorption (23°C / 50% RH) | 0.09 | % | ISO 62 |
| Water Absorption, (23°C/saturated) | 0.12 | % | ISO 62-1 |
| Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.8 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 120 | °C | ASTM D648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 116 | °C | ISO 75/Af |
| CTE, -40°C to 95°C, flow | 6.7E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 95°C, xflow | 8.E-05 | 1/°C | ASTM E831 |
| CTE, 23°C to 80°C, flow | 6.7E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate A/50 | 138 | °C | ASTM D1525 |
| Vicat Softening Temp, Rate B/50 | 138 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 139 | °C | ISO 306 |
| Relative Temp Index, Elec | 120 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 110 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 120 | °C | UL 746B |