LNP™ ELCRIN™ EXL9482RC

Sustainable Grade

LNP™ ELCRIN™ Compound EXL9482RC resin (also known as ELCRIN ER015586) is a medium flow, unfilled, non-brominated, non-chlorinated flame retardant, Polycarbonate (PC) siloxane copolymer, dark colors only, utilizing a minimum of 72% post-consumer recycle content. Added features of this material include: UL V-0 rating at 1.5 mm thickness.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Amorphous
Flame Retardant
Non Cl/Br flame retardant
Sustainable (Mechanical Recycling)

Industry

Material previously used in

Home Appliances

Applications

Possible usage of material

Electrical Components & Infrastructure
Electrical
Electronic Components
Game Player
Wireless Communications

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Constant
– 500 MHz	2.91	-	SABIC method
– 1 GHz	2.9	-	SABIC method
– 2.5 GHz	2.86	-	SABIC method
– 5 GHz	2.85	-	SABIC method
– 10 GHz	2.85	-	SABIC method
Dissipation Factor
– 500 MHz	0.02	-	SABIC method
– 1 GHz	0.009	-	SABIC method
– 2.5 GHz	0.015	-	SABIC method
– 5 GHz	0.015	-	SABIC method
– 10 GHz	0.003	-	SABIC method

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	1.5	mm	UL 94
Glow Wire Ignitability Temperature, 1.5 mm	825	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm	825	°C	IEC 60695-2-13
Glow Wire Flammability Index, 1.5 mm	960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 3.0 mm	960	°C	IEC 60695-2-12

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	800	J/m	ASTM D256
Izod Impact, notched, 0°C	660	J/m	ASTM D256
Izod Impact, notched, -20°C	470	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	228	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	53	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 0°C*	24.7	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -20°C*	16.1	kJ/m²	ISO 180/1A
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	300	kJ/m²	ISO 179/1eU
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	61	kJ/m²	ISO 179/1eA
*Charpy 0°C, V-notch Edgew 80103 sp=62mm*	26	kJ/m²	ISO 179/1eA
Instrumented Dart Impact Total Energy, 23°C	65	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 120	°C
Drying Time	3 - 4	Hrs
Drying Time (Cumulative)	8	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	295 - 315	°C
Rear - Zone 1 Temperature	270 - 295	°C
Middle - Zone 2 Temperature	280 - 305	°C
Front - Zone 3 Temperature	295 - 315	°C
Nozzle Temperature	290 - 310	°C
Mold Temperature	70 - 110	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	60	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	59	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5.8	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	150	%	ASTM D638
Nominal Strain, brk, 50 mm/min	90	%	ASTM D638
Tensile Modulus, 50 mm/min	2170	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	98	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2300	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	59.5	MPa	ISO 527
Tensile Stress, break, 50 mm/min	57	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5.8	%	ISO 527
Tensile Strain, break, 50 mm/min	150	%	ISO 527
Tensile Modulus, 1 mm/min	2170	MPa	ISO 527
Flexural Modulus, 2 mm/min	2270	MPa	ISO 178
Flexural Stress, yield, 2 mm/min	92	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Mold Shrinkage, flow	0.4 - 0.8	%	SABIC method
Mold Shrinkage, xflow	0.4 - 0.8	%	SABIC method
Melt Flow Rate, 300°C/1.2 kgf	12	g/10 min	ASTM D1238
Specific Gravity	1.2	-	ASTM D792

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	128	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	114.5	°C	ISO 75/Af
HDT, 0.45 MPa, 3.2 mm, unannealed	128	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	115	°C	ASTM D648
Vicat Softening Temp, Rate B/50	132	°C	ISO 306
Vicat Softening Temp, Rate B/120	134	°C	ISO 306
Vicat Softening Temp, Rate B/50	132	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	134	°C	ASTM D1525
CTE, -40°C to 40°C, flow	6.7E-5	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	7E-5	1/°C	ISO 11359-2
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES