LNP ELCRIN FXD141RG resin is transparent/translucent PC for light diffusion special effects. Color package may affect performance, that also incorporates renewable feedstock through ISCC+ mass-balance certification.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 1 | ≥3 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 2 | ≥1.14 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 2 | ≥1.5 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 3 | ≥1.14 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 2 | PLC Code | UL 746A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | ≥0.7 | mm | UL 94 |
| UV-light, water exposure/immersion | F2 | - | UL 746C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 854 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 76 | J | ASTM D3763 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 48 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 295 - 315 | °C | |
| Nozzle Temperature | 290 - 310 | °C | |
| Front - Zone 3 Temperature | 295 - 315 | °C | |
| Middle - Zone 2 Temperature | 280 - 305 | °C | |
| Rear - Zone 1 Temperature | 270 - 295 | °C | |
| Mold Temperature | 70 - 95 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Shot to Cylinder Size | 40 - 60 | % | |
| Vent Depth | 0.025 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 61 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 68 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 6.2 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 128 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2300 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 93 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2340 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.19 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate, 300°C/1.2 kgf | 10.8 | g/10 min | ASTM D1238 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 137 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 126 | °C | ASTM D648 |
| Relative Temp Index, Elec | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 130 | °C | UL 746B |