Sustainable Grade
LNP ELCRIN N1000DRCC compound is an unfilled polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) blend high heat plating grade containing 25% post-consumer recycled (PCR) PC. Available in limited colors.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 47 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 32 | kJ/m² | ISO 180/1A |
| Izod Impact, notched, 23°C | 540 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 470 | J/m | ASTM D256 |
| Instrumented Impact Total Energy, 23°C | 55 | J | ASTM D3763 |
| Charpy | |||
| – 23°C, V-notch Edgew 80*10*4 | 52 | kJ/m² | ISO 179/1eA |
| – -30°C, V-notch Edgew 80*10*4 | 39 | kJ/m² | ISO 179/1eA |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 100 - 105 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.04 | % | |
| Melt Temperature | 260 - 290 | °C | |
| Nozzle Temperature | 260 - 290 | °C | |
| Front - Zone 3 Temperature | 255 - 290 | °C | |
| Middle - Zone 2 Temperature | 255 - 290 | °C | |
| Rear - Zone 1 Temperature | 250 - 280 | °C | |
| Mold Temperature | 75 - 100 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Shot to Cylinder Size | 30 - 80 | % | |
| Vent Depth | 0.038 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 50 mm/min | 52 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 46 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4.9 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 70 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2100 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/min | 2200 | MPa | ISO 178 |
| Tensile Stress, yld, Type I, 50 mm/min | 56 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 47 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5.0 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 90 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2100 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 85 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2250 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 16 | cm³/10 min | ISO 1133 |
| Mold Shrinkage | |||
| – flow, 24 hrs | - | % | SABIC method |
| – xflow, 24 hrs | - | % | SABIC method |
| Melt Flow Rate, 260°C/5.0 kgf | 18 | g/10 min | ASTM D1238 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 128 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 109 | °C | ISO 75/Af |
| Vicat Softening Temp, Rate B/50 | 130 | °C | ASTM D1525 |
| Vicat Softening Temp, Rate B/120 | 131 | °C | ASTM D1525 |
| Vicat Softening Temp, Rate B/50 | 131 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 130 | °C | ISO 306 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 131 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 109 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 9.5E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 9.6E-05 | 1/°C | ASTM E831 |