Sustainable Grade
LNP ELCRIN N1000RCCG compound is an unfilled polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) blend medium heat plating grade containing 25% post-consumer recycled (PCR) PC and no intentionally added PFAS, that also incorporates renewable feedstock through ISCC+ mass-balance certification.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*3 -30°C | 27 | kJ/m² | ISO 180/1A |
| Instrumented Impact Total Energy, 23°C | 57 | J | ASTM D3763 |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 45 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 26 | kJ/m² | ISO 179/1eA |
| Izod Impact, notched, 23°C | 495 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 390 | J/m | ASTM D256 |
| Izod Impact, notched 80*10*3 +23°C | 41 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 95 - 105 | °C | |
| Drying Time | 2 - 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 250 - 280 | °C | |
| Nozzle Temperature | 230 - 270 | °C | |
| Front - Zone 3 Temperature | 240 - 280 | °C | |
| Middle - Zone 2 Temperature | 240 - 280 | °C | |
| Rear - Zone 1 Temperature | 220 - 250 | °C | |
| Mold Temperature | 60 - 90 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 50 mm/min | 49 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 42 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4.1 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 60 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2100 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 77 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2100 | MPa | ISO 178 |
| Tensile Stress, yld, Type I, 50 mm/min | 51 | MPa | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2000 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 47 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4.2 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 80 | % | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 78 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2100 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.1 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 12 | cm³/10 min | ISO 1133 |
| Mold Shrinkage, flow, 24 hrs | 0.7 - 0.8 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.7 - 0.8 | % | ASTM D955 |
| Melt Flow Rate, 260°C/2.16 kgf | 14 | g/10 min | ASTM D1238 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 120 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 98 | °C | ISO 75/Af |
| Vicat Softening Temp, Rate B/120 | 113 | °C | ASTM D1525 |
| Vicat Softening Temp, Rate B/50 | 111 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 112 | °C | ISO 306 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 117 | °C | ASTM D648 |
| Vicat Softening Temp, Rate B/50 | 111 | °C | ASTM D1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 96 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 1.0E-04 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 1.1E-04 | 1/°C | ASTM E831 |