RCX7236 is an impact modified Polycarbonate (PC) containing 60% PCR content with non-brominated and non-chlorinated FR intended for thin-wall applications requiring excellent impact/flow balance performance. It's available for custom color matching.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Recognized, 94V-0 Flame Class Rating | ≥1.0 | mm | UL 94 |
| Glow Wire Ignitability Temperature, 3.0 mm | 750 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 |
| UL Yellow Card Link | View | - | - |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 38 | kJ/m² | ISO 180/1A |
| Izod Impact, notched, 23°C | 650 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 120 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 61 | J | ASTM D3763 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 - 90 | °C | |
| Drying Time | 2 - 4 | Hrs | |
| Maximum Moisture Content | .02 | % | |
| Hopper Temperature | 60 - 80 | °C | |
| Melt Temperature | 250 - 300 | °C | |
| Rear - Zone 1 Temperature | 230 - 280 | °C | |
| Middle - Zone 2 Temperature | 240 - 290 | °C | |
| Front - Zone 3 Temperature | 250 - 300 | °C | |
| Nozzle Temperature | 250 - 300 | °C | |
| Mold Temperature | 60 - 85 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Modulus, 50 mm/min | 2500 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 100 | % | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 55 | MPa | ASTM D638 |
| Tensile Stress, yld, Type I, 50 mm/min | 65 | MPa | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2500 | MPa | ASTM D790 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 100 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Water Absorption, (23°C/saturated) | 0.12 | % | ISO 62-1 |
| Specific Gravity | 1.19 | - | ASTM D792 |
| Mold Shrinkage, flow | 0.4 - 0.6 | % | SABIC method |
| Melt Flow Rate, 260°C/2.16 kgf | 18 | g/10 min | ASTM D1238 |
| Melt Volume Rate, MVR at 260°C/2.16 kg | 16.8 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 90 | °C | ASTM D648 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 101 | °C | ASTM D648 |
| Vicat Softening Temp, Rate B/50 | 107 | °C | ASTM D1525 |
| CTE, -40°C to 40°C, flow | 7.5E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 7.5E-05 | 1/°C | ASTM E831 |
| Relative Temp Index, Elec | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |