LNP™ ELCRIN™ SLX2373RCC

Sustainable Grade

LNP ELCRIN ER016417 is based on Polycarbonate (PC) copolymer resin that offers enhanced UV stabilization and weatherable performance with 30% post consumer recycle (PCR) polycarbonate content. This medium flow (16 MVR) resin provides good processability for injection molding with added mold release. Targeted for potential paint elimination through a wide range of high gloss opaque colors and is also available in transparent colors or tints. ER016417 is targeted for broad range of automotive, building and construction, electrical, consumer and electronics applications.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Colorable
High gloss
IR Transparent
No PFAS intentionally added
Piano black
Sustainable (Mechanical Recycling)
Transparent/Translucent
Weatherable/UV stable

Industry

Material previously used in

Automotive Exteriors
Automotive Interiors
Building Component
Electrical
Lighting
Mobile Phone - Computer - Tablets
Personal Recreation
Recreational/Specialty Vehicles

Applications

Possible usage of material

automotive exterior
automotive exterior grille

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80103 +23°C*	66	kJ/m²	ISO 180/1A
*Izod Impact, notched 80103 -30°C*	10	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80103 +23°C*	NB	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	69	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80103 sp=62mm*	NB	kJ/m²	ISO 179/1eU
Izod Impact, notched, 23°C	750	J/m	ASTM D256
Izod Impact, notched, -30°C	150	J/m	ASTM D256
Multi-Axial Instrumented Impact Total Energy, 23°C	100	J	ISO 6603-2
Multi-Axial Instrumented Impact Energy @ peak, 23°C	95	J	ISO 6603-2
Instrumented Dart Impact Total Energy, 23°C	63	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	2 - 4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	280 - 310	°C
Rear - Zone 1 Temperature	260 - 280	°C
Middle - Zone 2 Temperature	270 - 290	°C
Front - Zone 3 Temperature	280 - 310	°C
Nozzle Temperature	270 - 290	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.3 - 0.7	MPa
Screw speed (Circumferential speed)	0.15 - 0.25	m/s

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 1 mm/min	2350	MPa	ISO 527
Tensile Stress, yield, 50 mm/min	64	MPa	ISO 527
Tensile Stress, break, 50 mm/min	68	MPa	ISO 527
Tensile Strain, break, 50 mm/min	>100	%	ISO 527
Flexural Modulus, 2 mm/min	2350	MPa	ISO 178
Flexural Stress, yield, 2 mm/min	97	MPa	ISO 178
Tensile Modulus, 50 mm/min	2400	MPa	ASTM D638
Tensile Stress, yld, Type I, 50 mm/min	67	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	66	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	6	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	>100	%	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	2400	MPa	ASTM D790
Flexural Stress, yld, 1.3 mm/min, 50 mm span	98	MPa	ASTM D790

OPTICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Light Transmission
– Light Transmission (2.51 mm)	88	-	ASTM D1003
– Haze (2.51 mm)	1.16	-	ASTM D1003
Refractive Index
– Refractive Index (589 nm)	1.59	-	SABIC method

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.21	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.1 - 0.2	%	ISO 62
Water Absorption, (23°C/saturated)	0.2 - 0.4	%	ISO 62-1
Mold Shrinkage, flow	0.5 - 0.7	%	SABIC method
Mold Shrinkage, xflow	0.5 - 0.7	%	SABIC method
Melt Volume Rate, MVR at 300°C/1.2 kg	16	cm³/10 min	ISO 1133
Specific Gravity	1.2	-	ASTM D792

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	122	°C	ISO 75/Af
HDT, 1.82 MPa, 3.2mm, unannealed	122	°C	ASTM D648
Vicat Softening Temp, Rate B/50	139	°C	ISO 306
Vicat Softening Temp, Rate B/120	139	°C	ISO 306
CTE, -40°C to 40°C, flow	7.0E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	7.0E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	Passes	-	IEC 60695-10-2

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES