Sustainable Grade
LNP ELCRIN W10001iQ compound is based on Polybutylene terephthalate (PBT) resin utilizing ELCRIN iQ upcycling technology containing minimum 44% Post-Consumer Recycling (PCR) weight content. Added features of this grade include: Non-Chlorinated, Non-Brominated Flame Retardant, Excellent Chemical Resistance and UL94V0 Flame Rating. This is a good candidate for a variety of applications needing a more sustainable FR and PBT solution.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-1 Flame Class Rating | 0.8 | mm | UL 94 |
| UL Recognized, 94V-0 Flame Class Rating | 1 | mm | UL 94 |
| UL Recognized, 94-5VA Flame Class Rating | ≥3 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 550 | J/m | ASTM D4812 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2 - 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 245 - 260 | °C | |
| Nozzle Temperature | 230 - 255 | °C | |
| Front - Zone 3 Temperature | 240 - 260 | °C | |
| Middle - Zone 2 Temperature | 235 - 250 | °C | |
| Rear - Zone 1 Temperature | 230 - 240 | °C | |
| Hopper Temperature | 40 - 60 | °C | |
| Mold Temperature | 40 - 100 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 41 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 10 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 2740 | MPa | ASTM D638 |
| Flexural Strength, 1.3 mm/min, 50 mm span | 66 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2430 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 20 | cm³/10 min | ISO 1133 |
| Mold Shrinkage on Tensile Bar, flow | 1.8 - 2.8 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 55 | °C | ASTM D648 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 150 | °C | ASTM D648 |
| Vicat Softening Temp, Rate A/50 | 208 | °C | ASTM D1525 |
| Vicat Softening Temp, Rate A/120 | 207 | °C | ASTM D1525 |
| Relative Temp Index, Elec | 150 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 100 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B |