Sustainable Grade
LNP ELCRIN W1000JiQ compound is based on Polybutylene terephthalate (PBT) resin utilizing ELCRIN iQ upcycling technology containing minimum 56% Post-Consumer Recycling (PCR) weight content. Added features of this grade include: Biocompatible (ISO10993), Improved Processing, Low Extractables, Healthcare. Applications include sprinklers, nozzles, pumps, cosmetic packages etc.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 50 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 46 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 61 | J | ASTM D3763 |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 2 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 12 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 245 - 260 | °C | |
| Nozzle Temperature | 240 - 255 | °C | |
| Front - Zone 3 Temperature | 245 - 260 | °C | |
| Middle - Zone 2 Temperature | 240 - 255 | °C | |
| Rear - Zone 1 Temperature | 230 - 250 | °C | |
| Mold Temperature | 50 - 75 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Shot to Cylinder Size | 40 - 80 | % | |
| Vent Depth | 0.013 - 0.025 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 56 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 29 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 3.2 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 140 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2550 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 84 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2560 | MPa | ASTM D790 |
| Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 50 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 3 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 130 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2550 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2430 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.31 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 1.6 - 2.4 | % | SABIC method |
| Melt Flow Rate, 250°C/2.16 kgf | 23 | g/10 min | ASTM D1238 |
| Density | 1.31 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.16 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 21 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 48 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 7.8E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 8.1E-05 | 1/°C | ASTM E831 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 133 | °C | ISO 75/Bf |
| Vicat Softening Temp, Rate B/120 | 168 | °C | ISO 306 |
| CTE, -40°C to 40°C, flow | 7.8E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 8.1E-05 | 1/°C | ISO 11359-2 |