Sustainable Grade
LNP™ ELCRIN W1000LiQ, utilizing ELCRIN iQ upcycling technology, is a general purpose, unreinforced iQ PBT resin. Added features included PCR content and improved processing. This grade contains minimum 56% PCR weight content and is based on food contact compliant ingredients. Applications include food handling, cosmetic packaging, razor blades, toothbrushes, etc.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 50 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 46 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 61 | J | ASTM D3763 |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 2 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 12 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 245 - 260 | °C | |
| Nozzle Temperature | 240 - 255 | °C | |
| Front - Zone 3 Temperature | 245 - 260 | °C | |
| Middle - Zone 2 Temperature | 240 - 255 | °C | |
| Rear - Zone 1 Temperature | 230 - 250 | °C | |
| Mold Temperature | 50 - 75 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 50 - 70 | rpm | |
| Shot to Cylinder Size | 40 - 80 | % | |
| Vent Depth | 0.013 - 0.025 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 56 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 29 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 3.2 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 140 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2550 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 84 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2560 | MPa | ASTM D790 |
| Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 50 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 3 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 130 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2550 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2430 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.31 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 1.6 - 2.4 | % | SABIC method |
| Melt Flow Rate, 250°C/2.16 kgf | 23 | g/10 min | ASTM D1238 |
| Density | 1.31 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.16 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 21 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 48 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 7.80E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 8.10E-05 | 1/°C | ASTM E831 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 133 | °C | ISO 75/Bf |
| Vicat Softening Temp, Rate B/120 | 168 | °C | ISO 306 |
| CTE, -40°C to 40°C, flow | 7.80E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 8.10E-05 | 1/°C | ISO 11359-2 |