LNP™ ELCRIN™ WF0061BiQ

Sustainable Grade

LNP ELCRIN WF0061BiQ is a 30% glass fiber reinforced, non-brominated, non-chlorinated flame-retardant Polybutylene Terephthalate (PBT) compound, utilizing iQ PBT chemical recycling process of Ocean Bound PET water bottles with minimum 26% ocean bound (OB) recycled content certified by UL 2809. Added features of this material include: good flow and UL V-0 rating at 0.8 mm thickness.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polybutylene Terephthalate (PBT)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Chemical Resistance
Flame Retardant
Good Processability
Heat Stabilized
High Flow
Non Cl/Br flame retardant
Sustainable (Advanced Recycling)

Industry

Material previously used in

Electrical
Material Handling
Personal Accessory

Applications

Possible usage of material

Electronics
Personal Computing
Thermoplastic
connector
evse
fan housing

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Hot-Wire Ignition (HWI), PLC 1	≥0.8	mm	UL 746A
Hot-Wire Ignition (HWI), PLC 0	≥3	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 0	≥0.8	mm	UL 746A
Comparative Tracking Index	600	V	IEC 60112

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	≥0.8	mm	UL 94
UL Recognized, 94-5VB Flame Class Rating	≥3.0	mm	UL 94
Glow Wire Ignitability Temperature, 3.0 mm	800	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 1.5 mm	775	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 0.8 mm	750	°C	IEC 60695-2-13
Glow Wire Flammability Index, 3.0 mm	960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 1.5 mm	960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 0.8 mm	960	°C	IEC 60695-2-12

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	540	J/m	ASTM D4812
Izod Impact, notched, 23°C	64	J/m	ASTM D256
Izod Impact, notched, -30°C	59	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	6	J	ASTM D3763
Instrumented Dart Impact Energy @ peak, 23°C	5	J	ASTM D3763
Instrumented Dart Impact Peak Force, 23°C	1200	N	ASTM D3763
*Izod Impact, unnotched 80104 +23°C*	39	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	8.5	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	8	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110 - 120	°C
Drying Time	2 - 4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	245 - 260	°C
Nozzle Temperature	230 - 255	°C
Front - Zone 3 Temperature	240 - 260	°C
Middle - Zone 2 Temperature	235 - 250	°C
Rear - Zone 1 Temperature	230 - 240	°C
Hopper Temperature	40 - 60	°C
Mold Temperature	40 - 100	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	104	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2	%	ASTM D638
Tensile Modulus, 5 mm/min	10800	MPa	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	165	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	10300	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	102	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2	%	ISO 527
Tensile Modulus, 1 mm/min	10720	MPa	ISO 527
Flexural Stress, break, 2 mm/min	162	MPa	ISO 178
Flexural Modulus, 2 mm/min	10570	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.57	-	ASTM D792
Melt Flow Rate, 250°C/5.0 kgf	24	g/10 min	ASTM D1238
Density	1.54	g/cm³	ISO 1183
Water Absorption, (23°C/24hrs)	0.08	%	ISO 62-1
Moisture Absorption, (23°C/50% RH/24hrs)	0.03	%	ISO 62-4
Melt Volume Rate, MVR at 250°C/5.0 kg	17	cm³/10 min	ISO 1133
Mold Shrinkage, flow	0.4	%	SABIC method
Mold Shrinkage, xflow	0.8	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	204	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	217	°C	ASTM D648
Vicat Softening Temp, Rate B/50	200	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	201	°C	ASTM D1525
CTE, -40°C to 40°C, flow	2.2E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	8.5E-05	1/°C	ASTM E831
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	202	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	217	°C	ISO 75/Bf
Ball Pressure Test, approximate maximum	175	°C	IEC 60695-10-2
Relative Temp Index, Elec	75	°C	UL 746B
Relative Temp Index, Mech w/impact	75	°C	UL 746B
Relative Temp Index, Mech w/o impact	75	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES