LNP™ ELCRIN™ WF006LXDiQ

Sustainable Grade

LNP ELCRIN WF006LXDiQ is based on an environmentally responsible and sustainable low carbon footprint resin. This grade contains a minimum of 37% PCR weight content. It is a glass fiber reinforced iQ PBT resin with excellent strength, stiffness, dimensional stability and heat resistance. Material may be suited for applications where food contact compliance is required. Restrictions may apply – please request a food contact declaration for details.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polybutylene Terephthalate (PBT)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Chemical Resistance
Dimensional stability
Food contact
High stiffness/Strength
No PFAS intentionally added
Sustainable (Advanced Recycling)

Industry

Material previously used in

Automotive Interiors
Commercial Appliance
Home Appliances
Home Decoration
Industrial Packaging
Mobile Phone - Computer - Tablets
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Personal Care
Small Appliance

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	630	J/m	ASTM D4812
Izod Impact, unnotched, -30°C	600	J/m	ASTM D4812
Izod Impact, notched, 23°C	73	J/m	ASTM D256
Izod Impact, notched, -30°C	74	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	49	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	41	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	8	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	8	kJ/m²	ISO 180/1A
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	54	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80104 sp=62mm*	48	kJ/m²	ISO 179/1eU
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	8	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	9	kJ/m²	ISO 179/1eA
Multi-Axial Instrumented Impact Total Energy, 23°C	8	J	ISO 6603-2
Multi-Axial Instrumented Impact Energy @ peak, 23°C	7	J	ISO 6603-2
Multi-Axial Instrumented Impact Total Energy, -30°C	6	J	ISO 6603-2
Multi-Axial Instrumented Impact Energy @ peak, -30°C	6	J	ISO 6603-2

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	2 - 4	Hrs
Drying Time (Cumulative)	12	Hrs
Maximum Moisture Content	0.05	%
Melt Temperature	240 - 265	°C
Nozzle Temperature	250 - 260	°C
Front - Zone 3 Temperature	260 - 270	°C
Middle - Zone 2 Temperature	245 - 255	°C
Rear - Zone 1 Temperature	220 - 230	°C
Mold Temperature	65 - 90	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	145	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	3	%	ASTM D638
Tensile Modulus, 5 mm/min	10500	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	205	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	8600	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	150	MPa	ISO 527
Tensile Strain, break, 5 mm/min	3	%	ISO 527
Tensile Modulus, 1 mm/min	10500	MPa	ISO 527
Flexural Strength, 2 mm/min	210	MPa	ISO 178
Flexural Modulus, 2 mm/min	9000	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.55	-	ASTM D792
Water Absorption, (23°C/24hrs)	<0.1	%	ASTM D570
Water Absorption, (23°C/Saturated)	0.6	%	ASTM D570
Density	1.55	g/cm³	ISO 1183
Moisture Absorption, (23°C/50% RH/24hrs)	<0.1	%	ISO 62-4
Moisture Absorption, (23°C/50% RH/Equilibrium)	<0.2	%	ISO 62-4
Water Absorption, (23°C/24hrs)	<0.1	%	ISO 62-1
Water Absorption, (23°C/saturated)	0.6	%	ISO 62-1
Melt Volume Rate, MVR at 250°C/5.0 kg	35	cm³/10 min	ISO 1133
Mold Shrinkage, flow, 3.2 mm	0.2 - 0.4	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	1 - 1.4	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	218	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	207	°C	ASTM D648
Vicat Softening Temp, Rate B/50	200	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	200	°C	ASTM D1525
CTE, 23°C to 60°C, flow	2.7E-05	1/°C	ASTM E831
CTE, 23°C to 60°C, xflow	1.4E-04	1/°C	ASTM E831
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	218	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	205	°C	ISO 75/Af
Vicat Softening Temp, Rate B/50	200	°C	ISO 306
Vicat Softening Temp, Rate B/120	200	°C	ISO 306
CTE, 23°C to 60°C, flow	2.7E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	1.4E-04	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	PASS	-	IEC 60695-10-2

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas