LNP™ ELCRIN™ WF006NAiQ

Sustainable Grade

LNP ELCRIN WF006NAiQ is an iQ PBT based compound containing 30% glass for NMT application. Added features of this material include: >25% PCR, high metal bonding strength, and good chemical resistance.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polybutylene Terephthalate (PBT)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Chemical Resistance
Dimensional stability
High Flow
High stiffness/Strength
Impact resistant
Nano molding technology
No PFAS intentionally added
Sustainable (Advanced Recycling)

Industry

Material previously used in

Electrical
Mobile Phone - Computer - Tablets
Personal Accessory

Applications

Possible usage of material

Auto Electrical
Personal Computing
Wireless Communications

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Constant, 1.1 GHz	3.65	-	SABIC method
Dissipation Factor, 1.1 GHz	0.015	-	SABIC method
Dielectric Constant, 1.9 GHz	3.69	-	SABIC method
Dissipation Factor, 1.9 GHz	0.014	-	SABIC method
Dielectric Constant, 5 GHz	3.66	-	SABIC method
Dissipation Factor, 5 GHz	0.013	-	SABIC method
Dielectric Constant, 10 GHz	3.64	-	SABIC method
Dissipation Factor, 10 GHz	0.011	-	SABIC method

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94HB Flame Class Rating	≥0.7	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	910	J/m	ASTM D4812
Izod Impact, notched, 23°C	150	J/m	ASTM D256
Izod Impact, notched, -30°C	110	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	51	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	14.5	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	11	kJ/m²	ISO 180/1A
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	56	kJ/m²	ISO 179/1eU
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	15	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	11	kJ/m²	ISO 179/1eA

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 120	°C
Drying Time	2 - 4	Hrs
Drying Time (Cumulative)	8	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	250 - 270	°C
Nozzle Temperature	245 - 275	°C
Front - Zone 3 Temperature	250 - 270	°C
Middle - Zone 2 Temperature	250 - 270	°C
Rear - Zone 1 Temperature	240 - 260	°C
Hopper Temperature	40 - 60	°C
Mold Temperature	100 - 160	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	113	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.7	%	ASTM D638
Tensile Modulus, 5 mm/min	8800	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	178	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	7770	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	111	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.6	%	ISO 527
Tensile Modulus, 1 mm/min	8700	MPa	ISO 527
Flexural Strength, 2 mm/min	173	MPa	ISO 178
Flexural Modulus, 2 mm/min	7400	MPa	ISO 178
Bonding Strength ("T" treatment, shear type)	32	MPa	ISO 19095

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Moisture Absorption, (23°C/50% RH/24hrs)	0.02	%	ISO 62-4
Water Absorption, (23°C/24hrs)	0.04	%	ISO 62-1
Density	1.48	g/cm³	ISO 1183
Melt Flow Rate, 250°C/5.0 kgf	12	g/10 min	ASTM D1238
Melt Flow Rate, 275°C/5 kgf	24	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 250°C/5.0 kg	9	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 275°C/5 kg	19	cm³/10 min	ISO 1133
Mold Shrinkage, flow	0.2 - 0.3	%	SABIC method
Mold Shrinkage, xflow	0.4 - 0.5	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Vicat Softening Temp, Rate B/50	150	°C	ASTM D1525
Vicat Softening Temp, Rate B/50	151	°C	ISO 306
HDT, 1.82 MPa, 3.2mm, unannealed	172	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	206	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	165	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	201	°C	ISO 75/Bf
CTE, -40°C to 40°C, flow	2.4E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	8.2E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	2.4E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	8.6E-05	1/°C	ISO 11359-2
Relative Temp Index, Elec	75	°C	UL 746B
Relative Temp Index, Mech w/impact	75	°C	UL 746B
Relative Temp Index, Mech w/o impact	75	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES