Sustainable Grade
LNP ELCRIN WF006NAiQ2 is an iQ PBT Generation 2 based compound containing 30% glass for NMT applications. Added features of this material include : >25% PCR, high flow, low warpage, high metal bonding strength and good chemical resistance.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Dielectric Constant | |||
| – 1.1 GHz | 3.60 | - | SABIC method |
| – 2.45 GHz | 3.60 | - | SABIC method |
| – 5 GHz | 3.58 | - | SABIC method |
| – 10 GHz | 3.58 | - | SABIC method |
| Dissipation Factor | |||
| – 1.1 GHz | 0.013 | - | SABIC method |
| – 2.45 GHz | 0.012 | - | SABIC method |
| – 5 GHz | 0.011 | - | SABIC method |
| – 10 GHz | 0.009 | - | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | ≥0.7 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Instrumented Dart Impact Total Energy, 23°C | 23 | J | ASTM D3763 |
| Instrumented Dart Impact Energy @ peak, 23°C | 12 | J | ASTM D3763 |
| Instrumented Dart Impact Peak Force, 23°C | 1600 | N | ASTM D3763 |
| Izod Impact, unnotched, 23°C | 831 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 138 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 95 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 +23°C | 70 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 11 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 2 - 4 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 250 - 270 | °C | |
| Nozzle Temperature | 245 - 275 | °C | |
| Front - Zone 3 Temperature | 250 - 270 | °C | |
| Middle - Zone 2 Temperature | 250 - 270 | °C | |
| Rear - Zone 1 Temperature | 240 - 260 | °C | |
| Hopper Temperature | 40 - 60 | °C | |
| Mold Temperature | 100 - 160 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 106 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.6 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 8240 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 163 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7320 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 110 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.6 | % | ISO 527 |
| Tensile Stress, yield, 5 mm/min | 111 | MPa | ISO 527 |
| Tensile Modulus, 1 mm/min | 8290 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/min | 7820 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 170 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Moisture Absorption, (23°C/50% RH/24hrs) | 0.02 | % | ISO 62-4 |
| Water Absorption, (23°C/24hrs) | 0.06 | % | ISO 62-1 |
| Specific Gravity | 1.53 | - | ASTM D792 |
| Density | 1.53 | g/cm³ | ISO 1183 |
| Melt Flow Rate, 250°C/5.0 kgf | 10 | g/10 min | ASTM D1238 |
| Melt Flow Rate, 275°C/5 kgf | 19 | g/10 min | ASTM D1238 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 8 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 275°C/5 kg | 14 | cm³/10 min | ISO 1133 |
| Mold Shrinkage, flow | 0.1 - 0.2 | % | SABIC method |
| Mold Shrinkage, xflow | 0.2 - 0.3 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/120 | 162 | °C | ASTM D1525 |
| Vicat Softening Temp, Rate B/50 | 158 | °C | ASTM D1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 161 | °C | ASTM D648 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 214 | °C | ASTM D648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 174 | °C | ISO 75/Af |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 216 | °C | ISO 75/Bf |
| CTE, -40°C to 40°C, flow | 2.3E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 1.4E-04 | 1/°C | ASTM E831 |
view multipoint data represented visually on graphs.