LNP™ ELCRIN™ WF006XXPiQ

Sustainable Grade

LNP ELCRIN WF006XXPiQ compound is based on Polybutylene terephthalate (PBT) resin utilizing ELCRIN iQ upcycling technology containing minimum 38% Post-Consumer Recycling (PCR) weight content and 30% pre-consumer recycled glass fiber. Total sustainable content 67%. Added features of this grade include Excellent Strength, Stiffness, Dimensional Stability and Colorable. Potential applications may include handles, connectors.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polybutylene Terephthalate (PBT)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Dimensional stability
High stiffness/Strength
No PFAS intentionally added
Sustainable (Advanced Recycling)

Industry

Material previously used in

Automotive Interiors
Commercial Appliance
Home Appliances
Home Decoration
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Personal Care
Small Appliance

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Constant, 2.5 GHz	3.58	-	SABIC method
Dissipation Factor, 2.5 GHz	0.008	-	SABIC method
Dielectric Constant, 5 GHz	3.61	-	SABIC method
Dissipation Factor, 5 GHz	0.008	-	SABIC method

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94HB Flame Class Rating	≥0.84	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	8	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	8	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	51	kJ/m²	ISO 180/1U
Izod Impact, unnotched, 23°C	810	J/m	ASTM D4812
Izod Impact, notched, 23°C	84	J/m	ASTM D256
Izod Impact, notched, -30°C	73	J/m	ASTM D256
Instrumented Impact Total Energy, 23°C	8	J	ASTM D3763
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	8	kJ/m²	ISO 179/1eA

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	3 - 4	Hrs
Drying Time (Cumulative)	12	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	250 - 265	°C
Nozzle Temperature	245 - 265	°C
Front - Zone 3 Temperature	250 - 265	°C
Middle - Zone 2 Temperature	245 - 260	°C
Rear - Zone 1 Temperature	240 - 255	°C
Mold Temperature	65 - 90	°C
Back pressure (Plastic Pressure)	0.3 - 0.7	MPa
Screw Speed	50 - 80	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break, 5 mm/min	134	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.6	%	ISO 527
Tensile Modulus, 1 mm/min	10500	MPa	ISO 527
Flexural Stress, break, 2 mm/min	196	MPa	ISO 178
Flexural Modulus, 2 mm/min	9200	MPa	ISO 178
Tensile Stress, brk, Type I, 5 mm/min	137	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.8	%	ASTM D638
Tensile Modulus, 5 mm/min	10700	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	207	MPa	ASTM D790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	202	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	9400	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.59	g/cm³	ISO 1183
Moisture Content	0.02	%	SABIC method
Melt Volume Rate, MVR at 250°C/5.0 kg	35	cm³/10 min	ISO 1133
Specific Gravity	1.60	-	ASTM D792
Mold Shrinkage, flow	0.4 - 0.6	%	SABIC method
Mold Shrinkage, xflow	0.9 - 1.1	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	213	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	196	°C	ISO 75/Af
Vicat Softening Temp, Rate B/50	206	°C	ASTM D1525
Vicat Softening Temp, Rate B/50	204	°C	ISO 306
HDT, 0.45 MPa, 3.2 mm, unannealed	214	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	201	°C	ASTM D648
CTE, -40°C to 40°C, flow	2.3E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	9.3E-05	1/°C	ASTM E831

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES