LNP™ ELCRIN™ WF008NiQ

Sustainable Grade

LNP ELCRIN WF008NiQ is an iQ PBT/glass fiber compound for nano-molding technology (NMT) application. Added features of this material include: >20% PCR content, high modulus, excellent metal bonding force, good surface quality, high impact, good adhesion and good color stability during anodizing process.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polybutylene Terephthalate (PBT)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Chemical Resistance
Electroplatable
High Flow
High stiffness/Strength
Impact resistant
Nano molding technology
No PFAS intentionally added
Sustainable (Advanced Recycling)

Industry

Material previously used in

Personal Accessory

Applications

Possible usage of material

Displays
Electrical Components & Infrastructure
Electrical
nmt
nano molding technology
mobile phone antenna
laptop antenna
wearable device antenna
antenna split

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Constant, 1.1 GHz	3.9	-	SABIC method
Dissipation Factor, 1.1 GHz	0.0118	-	SABIC method
Dielectric Constant, 1.9 GHz	3.88	-	SABIC method
Dissipation Factor, 1.9 GHz	0.0115	-	SABIC method
Dielectric Constant, 5 GHz	3.91	-	SABIC method
Dissipation Factor, 5 GHz	0.0105	-	SABIC method
Dielectric Constant, 10 GHz	3.84	-	SABIC method
Dissipation Factor, 10 GHz	0.0095	-	SABIC method
Dielectric Constant, 20 GHz	3.78	-	SABIC method
Dissipation Factor, 20 GHz	0.0112	-	SABIC method

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94HB Flame Class Rating	≥0.7	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	160	J/m	ASTM D256
Izod Impact, notched, -30°C	135	J/m	ASTM D256
Izod Impact, unnotched, 23°C	1000	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	15	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	14	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	53	kJ/m²	ISO 180/1U
Charpy Impact, notched, 23°C	15.5	kJ/m²	ISO 179/2C
Charpy Impact, notched, -30°C	14.5	kJ/m²	ISO 179/2C
Charpy Impact, unnotched, 23°C	63	kJ/m²	ISO 179/2C

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 120	°C
Drying Time	2 - 4	Hrs
Maximum Moisture Content	0.02	%
Hopper Temperature	40 - 60	°C
Melt Temperature	250 - 270	°C
Nozzle Temperature	255 - 275	°C
Front - Zone 3 Temperature	250 - 275	°C
Middle - Zone 2 Temperature	250 - 275	°C
Rear - Zone 1 Temperature	240 - 260	°C
Mold Temperature	100 - 150	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	150	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.6	%	ASTM D638
Tensile Modulus, 5 mm/min	13200	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	165	MPa	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	2.8	%	ASTM D638
Tensile Modulus, 50 mm/min	13200	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	225	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	10900	MPa	ASTM D790
Tensile Modulus, 1 mm/min	13000	MPa	ISO 527
Tensile Stress, break, 5 mm/min	151	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.5	%	ISO 527
Tensile Stress, break, 50 mm/min	162	MPa	ISO 527
Tensile Strain, break, 50 mm/min	2.6	%	ISO 527
Flexural Strength, 2 mm/min	223	MPa	ISO 178
Flexural Modulus, 2 mm/min	11000	MPa	ISO 178
Bonding Strength ("T" treatment, shear type)	34	MPa	ISO 19095
Bonding strength (TRI) , 5 mm/min, Type A	38	MPa	ISO 19095

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.6	g/cm³	ISO 1183
Water Absorption, (23°C/24hrs)	0.03	%	ISO 62-1
Moisture Absorption, (23°C/50% RH/24hrs)	0.01	%	ISO 62-4
Melt Flow Rate, 275°C/2.16 kgf	11	g/10 min	ASTM D1238
Melt Flow Rate, 275°C/5 kgf	39	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 275°C/2.16 kg	10	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 275°C/5 kg	30	cm³/10 min	ISO 1133
Mold Shrinkage, flow	0.2	%	SABIC method
Mold Shrinkage, xflow	0.5	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	217	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	206	°C	ASTM D648
HDT, 1.82 MPa, 6.4 mm, unannealed	207	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	218	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	206	°C	ISO 75/Af
CTE, -40°C to 40°C, flow	1.9E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	6.4E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	1.8E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	6.8E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	200	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	198	°C	ASTM D1525
Vicat Softening Temp, Rate B/50	201	°C	ISO 306
Vicat Softening Temp, Rate B/120	196	°C	ISO 306
Relative Temp Index, Elec	75	°C	UL 746B
Relative Temp Index, Mech w/impact	75	°C	UL 746B
Relative Temp Index, Mech w/o impact	75	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES