Sustainable Grade
LNP™ ELCRIN™ XSR8243RCC Copolymer is an injection moldable, polycarbonate copolymer blend having excellent scratch & mar durability with 30% post-consumer recycle (PCR) polycarbonate. This medium flow resin is UV stabilized and provides good processability for injection molding in combination with balanced physical properties and is available in a wide range of high gloss, opaque colors. It is targeted for potential paint elimination in automotive interior parts, consumer and electronics applications.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 500 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | NB | J/m | ASTM D4812 |
| Izod Impact, notched 80*10*4 +23°C | 46 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 10 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 46 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 75 - 85 | °C | |
| Drying Time | 6 | Hrs | |
| Maximum Moisture Content | 0.01 | % | |
| Hopper Temperature | 40 - 60 | °C | |
| Melt Temperature | 240 - 280 | °C | |
| Rear - Zone 1 Temperature | 220 - 260 | °C | |
| Middle - Zone 2 Temperature | 230 - 270 | °C | |
| Front - Zone 3 Temperature | 240 - 280 | °C | |
| Nozzle Temperature | 250 - 280 | °C | |
| Mold Temperature | 80 - 110 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 60 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 50 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 38 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2300 | MPa | ASTM D638 |
| Flexural Strength, 1.3 mm/min, 50 mm span | 90 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2400 | MPa | ASTM D790 |
| Tensile Stress, yield, 50 mm/min | 60 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 50 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 37 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2300 | MPa | ISO 527 |
| Flexural Strength, 2 mm/min | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2400 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.16 | - | ASTM D792 |
| Mold Shrinkage, flow | 0.5 - 0.75 | % | SABIC method |
| Mold Shrinkage, xflow | 0.5 - 0.75 | % | SABIC method |
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 15 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 104 | °C | ISO 75/Af |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 124 | °C | ISO 75/Bf |
| HDT, 1.82 MPa, 3.2mm, unannealed | 104 | °C | ASTM D648 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 124 | °C | ASTM D648 |
| Vicat Softening Temp, Rate B/120 | 124 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 124 | °C | ASTM D1525 |
| CTE, -40°C to 40°C, flow | 7.2E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.8E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, flow | 7.2E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 7.8E-05 | 1/°C | ASTM E831 |