LNP FARADEX AS004 compound is based on Acrylonitrile Butadiene Styrene (ABS) resin containing 20% stainless steel fiber. Added features of this grade include: Electrically Conductive, EMI/RFI shielding.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+01 - 1.E+03 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.05 - 0.1 | % | |
| Melt Temperature | 240 - 255 | °C | |
| Front - Zone 3 Temperature | 255 - 265 | °C | |
| Middle - Zone 2 Temperature | 230 - 245 | °C | |
| Rear - Zone 1 Temperature | 210 - 220 | °C | |
| Mold Temperature | 70 - 95 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 5 mm/min | 44 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3400 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 60 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3100 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar, flow | 0.3 - 0.5 | % | SABIC method |
| Density | 1.17 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 98 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 86 | °C | ISO 75/Af |