LNP FARADEX DS0026IX2 compound is based on Polycarbonate (PC) resin containing stainless steel fiber. Added features of this grade include: Electrically Conductive, EMI/RFI shielding, High Impact, Non-Brominated & Non-Chlorinated Flame Retardant, UL f1/V-0/5VA rating for a limited range of colors.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Volume Resistivity | 1.E+04 - 1.E+06 | Ω.cm | ASTM D257 |
| Surface Resistivity | 1.E+02 - 1.E+04 | Ω | ASTM D257 |
| Static Decay, 5000V to <50V | <0.01 | Seconds | FTMS101B |
| Shielding Effectivness @ 3mm | 40 - 55 | dB | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Recognized, 94-5VA Flame Class Rating | ≥3.0 | mm | UL 94 |
| UL Recognized, 94V-0 Flame Class Rating | ≥2.0 | mm | UL 94 |
| UL Recognized, 94V-1 Flame Class Rating | ≥1.6 | mm | UL 94 |
| UV-light, water exposure/immersion | F1 | - | UL 746C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 1790 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 124 | J/m | ASTM D256 |
| Izod Impact, notched, -40°C | 80 | J/m | ASTM D256 |
| Multiaxial Impact | 29 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 85 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 14 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -40°C | 11 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 305 - 325 | °C | |
| Front - Zone 3 Temperature | 320 - 330 | °C | |
| Middle - Zone 2 Temperature | 310 - 320 | °C | |
| Rear - Zone 1 Temperature | 295 - 305 | °C | |
| Mold Temperature | 95 - 120 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 59 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 53 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 4.3 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 5.1 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 2550 | MPa | ASTM D638 |
| Tensile Stress, yield, 5 mm/min | 57 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 55 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3.8 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 4.8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2800 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2600 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar, flow | 0.4 - 0.7 | % | SABIC method |
| Mold Shrinkage, xflow, 24 hrs | 0.4 - 0.6 | % | ISO 294 |
| Density | 1.29 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/24hrs) | 0.13 | % | ISO 62-1 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 60°C, flow | 5.7E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 6.8E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 136 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 125 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 110 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 115 | °C | UL 746B |