LNP™ FARADEX™ Compound MS003

LNP FARADEX MS003 compound is based on Polypropylene (PP) resin containing 15% stainless steel fiber. Added features of this grade include: Electrically Conductive, EMI/RFI shielding.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polypropylene, Unspecified (PP, Unspecified)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Electrically Conductive
EMI/RFI Shielding
No PFAS intentionally added

Industry

Material previously used in

Commercial Appliance
Electrical
Electronic Components
Industrial Packaging
Material Handling

Applications

Possible usage of material

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	1.E+04	Ω.cm	ASTM D257
Surface Resistivity	1.E+03	Ω	ASTM D257
Static Decay, 5000V to <50V	<0.01	Seconds	FTMS101B
Shielding Effectivness @ 3mm	50 - 65	dB	SABIC method

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	1226	J/m	ASTM D4812
Izod Impact, notched, 23°C	267	J/m	ASTM D256
Multiaxial Impact	22	J	ISO 6603
*Izod Impact, unnotched 80104 +23°C*	80	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	25	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Melt Temperature	230 - 250	°C
Front - Zone 3 Temperature	260 - 270	°C
Middle - Zone 2 Temperature	230 - 245	°C
Rear - Zone 1 Temperature	205 - 215	°C
Mold Temperature	30 - 55	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	25 - 50	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield	19	MPa	ASTM D638
Tensile Stress, break	15	MPa	ASTM D638
Tensile Strain, yield	6.2	%	ASTM D638
Tensile Strain, break	88.4	%	ASTM D638
Tensile Modulus, 50 mm/min	1190	MPa	ASTM D638
Flexural Stress	27	MPa	ASTM D790
Flexural Modulus	1190	MPa	ASTM D790
Tensile Stress, yield	21	MPa	ISO 527
Tensile Stress, break	15	MPa	ISO 527
Tensile Strain, yield	5.2	%	ISO 527
Tensile Strain, break	72	%	ISO 527
Tensile Modulus, 1 mm/min	1300	MPa	ISO 527
Flexural Stress	32	MPa	ISO 178
Flexural Modulus	1500	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.01	g/cm³	ASTM D792
Mold Shrinkage, flow, 24 hrs	1.2	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	1.3	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	1.2	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.3	%	ISO 294
Density	1.01	g/cm³	ISO 1183
Water Absorption, (23°C/24hrs)	0.03	%	ISO 62-1

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	92	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	53	°C	ASTM D648
CTE, -40°C to 40°C, flow	1.04E-04	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	9.72E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	1.43E-04	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	1.7E-04	1/°C	ISO 11359-2
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	95	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	56	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES