LNP™ FARADEX™ Compound NS003

LNP FARADEX NS003 compound is based on Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend containing 15% stainless steel fiber. Added features of this grade include: Electrically Conductive, EMI/RFI shielding.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate + ABS (PC+ABS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Electrically Conductive
EMI/RFI Shielding
No PFAS intentionally added

Industry

Material previously used in

Commercial Appliance
Electrical
Electronic Components
Industrial Packaging
Material Handling

Applications

Possible usage of material

Antenna
Cluster
Data Management
Enclosure/Housing/Cover
Enclosures
Medical Device
Semiconductor
metal replacement
adas
emi shielding
rfi shielding
atex
ecu
ecm
radar
transceiver
walkie talkie
camera
cross talk reduction
electrically conductive
navigation device
business equipment

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	1.E+04	Ω.cm	ASTM D257
Surface Resistivity	1.E+01 - 1.E+03	Ω	ASTM D257
Static Decay, 5000V to <50V	<0.01	Seconds	FTMS101B
Shielding Effectivness @ 3mm	50 - 65	dB	SABIC method

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	9	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	32	kJ/m²	ISO 180/1U
Izod Impact, notched, 23°C	74	J/m	ASTM D256
Izod Impact, unnotched, 23°C	573	J/m	ASTM D4812
Instrumented Dart Impact Energy @ peak, 23°C	15	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	220 - 260	°C
Front - Zone 3 Temperature	245 - 255	°C
Middle - Zone 2 Temperature	230 - 245	°C
Rear - Zone 1 Temperature	220 - 230	°C
Mold Temperature	40 - 80	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield	50	MPa	ISO 527
Tensile Stress, break	46	MPa	ISO 527
Tensile Strain, yield	3.5	%	ISO 527
Tensile Strain, break	6	%	ISO 527
Tensile Modulus, 1 mm/min	2700	MPa	ISO 527
Flexural Stress	86	MPa	ISO 178
Flexural Modulus	2800	MPa	ISO 178
Tensile Stress, yield	52	MPa	ASTM D638
Tensile Stress, break	49	MPa	ASTM D638
Tensile Strain, yield	3.3	%	ASTM D638
Tensile Strain, break	4.7	%	ASTM D638
Tensile Modulus, 50 mm/min	3100	MPa	ASTM D638
Flexural Stress	89	MPa	ASTM D790
Flexural Modulus	2990	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.21	g/cm³	ISO 1183
Mold Shrinkage, flow, 24 hrs	0.3	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.35	%	ISO 294
Density	1.24	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.1	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.3	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.35	%	ASTM D955

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	103	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	115	°C	ISO 75/Bf
CTE, -40°C to 40°C, flow	5.90E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	8.20E-05	1/°C	ISO 11359-2
HDT, 0.45 MPa, 3.2 mm, unannealed	120	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	105	°C	ASTM D648
CTE, -40°C to 40°C, flow	6.30E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	7.74E-05	1/°C	ASTM E831

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES